'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
EAA PRIMACOR™ 1430 STYRON US
424
- Unit Price:US$ 3,530 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Blow molding grade
Technical Data Sheet
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | 45°，50.8um | ASTM D-2457 | 74 |
| turbidity | 50.8um | ISO 14782 | 4 % |
| 50.8um | ASTM D-1003 | 4 % | |
| gloss | 45°,50.8μm | ASTM D2457 | 74 |
| turbidity | 50.8μm | ASTM D1003 | 4.0 % |
| 50.8μm | ISO 14782 | 4.0 % |
| Basic Performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 190℃/2.16kg | ASTM D-1238 | 5 g/10min |
| 190℃/2.16kg | ISO 1133 | 5 g/10min | |
| Monomer content | Internal Method | 9.7 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Elongation at Break | 50.8um，MD | ASTM D-882 | 420 % |
| 50.8um，TD | ASTM D-882 | 470 % | |
| 50.8um，TD | ISO 527-3 | 470 % | |
| 50.8um，MD | ISO 527-3 | 420 % | |
| Elmendorf tear strength | 50.8um，MD | ASTM D-1922 | 470 g |
| 50.8um，TD | ASTM D-1922 | 730 g | |
| 50.8um，MD | ISO 6383-2 | 2100 N | |
| 50.8um，TD | ISO 6383-2 | 3300 N | |
| tensile strength | Yield,Compression Molded | ASTM D-638 | 7.67 MPa |
| Yield,Compression Molded | ISO 527-2/508 | 7.67 MPa | |
| Compression Molded，Break | ASTM D-638 | 19.5 MPa | |
| Compression Molded，Break | ISO 527-2/508 | 19.5 MPa | |
| Elongation at Break | Compression Molded | ASTM D-638 | 580 % |
| Compression Molded | ISO 527-2/508 | 580 % | |
| tensile strength | 50.8um，Yield,MD | ASTM D-882 | 10.4 MPa |
| 50.8um，Yield,TD | ASTM D-882 | 10.2 MPa | |
| 50.8um，Yield,MD | ISO 527-3 | 10.4 MPa | |
| 50.8um，Yield,TD | ISO 527-3 | 10.2 MPa | |
| 50.8um，TD,Break | ASTM D-882 | 31.0 MPa | |
| 50.8um，MD,Break | ASTM D-882 | 30.6 MPa | |
| 50.8um，TD,Break | ISO 527-3 | 31 MPa | |
| 50.8um，MD,Break | ISO 527-3 | 30.6 MPa | |
| Yield,Compression Molded4 | ASTM D638 | 7.67 Mpa | |
| Yield,Compression Molded | ISO 527-2/508 | 7.67 Mpa | |
| Break,Compression Molded4 | ASTM D638 | 19.5 Mpa | |
| Break,Compression Molded | ISO 527-2/508 | 19.5 Mpa | |
| elongation | Break,Compression Molded4 | ASTM D638 | 580 % |
| Break,Compression Molded | ISO 527-2/508 | 580 % |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Vicat softening temperature | ASTM D-1525 | 76.1 ℃ | |
| ISO 306 | 76.1 ℃ | ||
| Melting temperature | Internal Method | 96.1 ℃ | |
| Vicat softening temperature | ASTMD1525 | 76.1 °C | |
| Melting temperature | Internal Method | 96.1 °C |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D-792 | 0.93 g/cm³ | |
| ISO 1183 | 0.93 g/cm³ | ||
| ASTMD792 | 0.930 g/cm³ | ||
| melt mass-flow rate | 190°C/2.16kg | ASTMD1238 | 5.0 g/10min |
| Content of comonomer | Internal Method | 9.7 % |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Elmendorf tear strength | MD:51μm | ASTM D1922 | 470 g |
| TD:51μm | ASTM D1922 | 730 g | |
| MD:51μm | ISO 6383-2 | 2100 N | |
| TD:51μm | ISO 6383-2 | 3300 N | |
| tensile strength | MD:Yield,51μm | ASTM D882 | 10.4 Mpa |
| TD:Yield,51μm | ASTM D882 | 10.2 Mpa | |
| MD:Yield,51μm | ISO 527-3 | 10.4 Mpa | |
| TD:Yield,51μm | ISO 527-3 | 10.2 Mpa | |
| MD:Break,51μm | ASTMD882 | 30.6 Mpa | |
| TD:Break,51μm | ASTMD882 | 31.0 Mpa | |
| elongation | MD:Break,51μm | ASTMD882 | 420 % |
| TD:Break,51μm | ASTMD882 | 470 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.