PC LNP™ THERMOCOMP™ D251-701 SABIC INNOVATIVE US
165
- Unit Price:US$ 4,349 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:45MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Non chloro non bromine flame retardant｜Glass fiber reinforced
- Application Areas:Electronic and Electrical Applications｜Plastic bag
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 121 °C |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 116 °C | |
| Linear coefficient of thermal expansion | MD:23到80°C | ISO 11359-2 | 2.6E-05 cm/cm/°C |
| TD:23到80°C | ISO 11359-2 | 7.3E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.500mm | UL 94 | V-1 |
| 0.600mm | UL 94 | V-0 | |
| 0.300mm | UL 94 | V-2 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 14 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 51 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 720 J/m |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 22.0 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 17 g/10min |
| 300°C/2.16kg | ASTM D1238 | 33 g/10min | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 15.0 cm3/10min |
| 300°C/2.16kg | ISO 1133 | 29.0 cm3/10min | |
| shrinkage rate | MD:24小时 | ASTM D955 | 0.20-0.40 % |
| TD:24小时 | ASTM D955 | 0.20-0.40 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.070 % |
| 平衡,23°C,50%RH | ISO 62 | 0.030 % | |
| density | ASTM D792 | 1.35 g/cm³ |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | 1.90GHz | 内部方法 | 3.20 |
| 5.00GHz | 内部方法 | 3.20 | |
| 10.0GHz | 内部方法 | 3.20 | |
| 20.0GHz | 内部方法 | 3.20 | |
| Dissipation Factor | 1.10GHz | 内部方法 | 6.3E-03 |
| 1.90GHz | 内部方法 | 6.3E-03 | |
| 5.00GHz | 内部方法 | 6.4E-03 | |
| 10.0GHz | 内部方法 | 6.7E-03 | |
| 20.0GHz | 内部方法 | 6.5E-03 | |
| dielectric constant | 1.10GHz | 内部方法 | 3.20 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| --1 | ASTM D638 | 6680 Mpa | |
| fracture | ASTM D638 | 110 Mpa | |
| ISO 527-2/5 | 112 Mpa | ||
| ASTM D638 | 2.7 % | ||
| ISO 527-2/5 | 2.6 % | ||
| 50.0mm span | ASTM D790 | 6150 Mpa | |
| --5 | ISO 178 | 6240 Mpa | |
| --6 | ISO 178 | 165 Mpa | |
| Fracture, 50.0mm span | ASTM D790 | 167 Mpa | |
| --1 | ASTM D638 | 6680 Mpa | |
| fracture | ASTM D638 | 110 Mpa | |
| ISO 527-2/5 | 112 Mpa | ||
| ASTM D638 | 2.7 % | ||
| ISO 527-2/5 | 2.6 % | ||
| 50.0mm span | ASTM D790 | 6150 Mpa | |
| --5 | ISO 178 | 6240 Mpa | |
| --6 | ISO 178 | 165 Mpa | |
| Fracture, 50.0mm span | ASTM D790 | 167 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.