Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC D251-701 SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Electronic and Electrical Applications,Plastic bag
Non chloro non bromine fl,Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/D251-701 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 14 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 22.0 J |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 51 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 720 J/m |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/D251-701 |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 121 °C |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 116 °C | |
| Linear coefficient of thermal expansion | TD:23到80°C | ISO 11359-2 | 7.3E-05 cm/cm/°C |
| MD:23到80°C | ISO 11359-2 | 2.6E-05 cm/cm/°C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/D251-701 |
|---|---|---|---|
| --1 | ASTM D638 | 6680 Mpa | |
| --5 | ISO 178 | 6240 Mpa | |
| 50.0mm span | ASTM D790 | 6150 Mpa | |
| --6 | ISO 178 | 165 Mpa | |
| fracture | ASTM D638 | 110 Mpa | |
| ASTM D638 | 2.7 % | ||
| ISO 527-2/5 | 2.6 % | ||
| ISO 527-2/5 | 112 Mpa | ||
| Fracture, 50.0mm span | ASTM D790 | 167 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/D251-701 |
|---|---|---|---|
| dielectric constant | 1.90GHz | 内部方法 | 3.20 |
| 20.0GHz | 内部方法 | 3.20 | |
| 1.10GHz | 内部方法 | 3.20 | |
| 10.0GHz | 内部方法 | 3.20 | |
| 5.00GHz | 内部方法 | 3.20 | |
| Dissipation Factor | 5.00GHz | 内部方法 | 6.4E-03 |
| 1.90GHz | 内部方法 | 6.3E-03 | |
| 10.0GHz | 内部方法 | 6.7E-03 | |
| 1.10GHz | 内部方法 | 6.3E-03 | |
| 20.0GHz | 内部方法 | 6.5E-03 |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/D251-701 |
|---|---|---|---|
| density | ASTM D792 | 1.35 g/cm³ | |
| melt mass-flow rate | 300°C/2.16kg | ASTM D1238 | 33 g/10min |
| 300°C/1.2kg | ASTM D1238 | 17 g/10min | |
| Melt volume flow rate | 300°C/2.16kg | ISO 1133 | 29.0 cm3/10min |
| 300°C/1.2kg | ISO 1133 | 15.0 cm3/10min | |
| shrinkage rate | TD:24小时 | ASTM D955 | 0.20-0.40 % |
| MD:24小时 | ASTM D955 | 0.20-0.40 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.070 % |
| 平衡,23°C,50%RH | ISO 62 | 0.030 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/D251-701 |
|---|---|---|---|
| UL flame retardant rating | 0.600mm | UL 94 | V-0 |
| 0.500mm | UL 94 | V-1 | |
| 0.300mm | UL 94 | V-2 |