PC/ABS

PC/ABS CYCOLOY™ MC1300-100 SABIC INNOVATIVE CHONGQING

219

Unit Price:US$ 3,165 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance｜High mobility｜Easy electroplating
Application Areas:Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C, Total Energy	ASTM D3763	40.0 J
Dart impact	Dart impact	-30°C, Total Energy	ASTM D3763	33.0 J

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield, 50.0 mm Span	ASTM D790	72.0 Mpa
Bending modulus	50.0 mm Span	ASTM D790	2060 Mpa
elongation	Break	ASTM D638	150 %
elongation	elongation	Yield	ASTM D638	8.6 %
tensile strength	Break	ASTM D638	44.0 Mpa
tensile strength	tensile strength	Yield	ASTM D638	50.0 Mpa
Tensile modulus		ASTM D638	2130 Mpa

injection	Test Condition	Test Method	Test Result
Temperature in the middle of the barrel			255 to 290 °C
Temperature at the rear of the barrel			250 to 280 °C
Suggested injection volume			30 to 80 %
Suggested maximum moisture content			0.020 %
drying time			3.0 to 4.0 hr
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 70 rpm
Exhaust hole depth			0.038 to 0.076 mm
drying temperature			100 to 105 °C
Temperature at the front of the material cylinder			255 to 290 °C
Spray nozzle temperature			260 to 290 °C
Processing (melt) temperature			260 to 290 °C
Mold temperature			75 to 100 °C

thermal performance	Test Condition	Test Method	Test Result
thermal conductivity		ASTM C177	0.20 W/m/K
Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	9.0E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.2E-5 cm/cm/°C
Vicat softening temperature		ASTM D15255	111 °C
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	98.0 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	115 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	24 hr	ASTM D570	0.10 %
Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.50 - 0.70 %
Shrinkage rate	Shrinkage rate	Flow : 3.20 mm	Internal Method	0.50 - 0.80 %
melt mass-flow rate	260°C/5.0 kg	ASTM D1238	14 g/10 min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/ABS CYCOLOY™ MC1300-100 SABIC INNOVATIVE CHONGQING

Material Description

Technical Data Sheet Compare

Technical Data Sheet