Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS MC1300-100 SABIC INNOVATIVE CHONGQING
CYCOLOY™
Automotive sector
High impact resistance、High mobility、Easy electroplating
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/MC1300-100 |
|---|---|---|---|
| Dart impact | -30°C, Total Energy | ASTM D3763 | 33.0 J |
| 23°C, Total Energy | ASTM D3763 | 40.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/MC1300-100 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2130 Mpa | |
| elongation | 断裂 | ASTM D638 | 150 % |
| 屈服 | ASTM D638 | 8.6 % | |
| bending strength | 屈服, 50.0 mm 跨距 | ASTM D790 | 72.0 Mpa |
| tensile strength | 断裂 | ASTM D638 | 44.0 Mpa |
| 屈服 | ASTM D638 | 50.0 Mpa | |
| Flexural modulus | 50.0 mm 跨距 | ASTM D790 | 2060 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/MC1300-100 |
|---|---|---|---|
| Shrinkage rate | 横向流动 : 3.20 mm | 内部方法 | 0.50 - 0.70 % |
| Water absorption rate | 24 hr | ASTM D570 | 0.10 % |
| Shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.50 - 0.80 % |
| melt mass-flow rate | 260°C/5.0 kg | ASTM D1238 | 14 g/10 min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/MC1300-100 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 7.2E-5 cm/cm/°C |
| thermal conductivity | ASTM C177 | 0.20 W/m/K | |
| vicat | ASTM D15255 | 111 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 115 °C |
| Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 9.0E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 98.0 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE CHONGQING/MC1300-100 |
|---|---|---|---|
| screw speed | 40 to 70 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Processing (melt) temperature | 260 to 290 °C | ||
| drying temperature | 100 to 105 °C | ||
| Suggested injection volume | 30 to 80 % | ||
| drying time | 3.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 255 to 290 °C | ||
| Temperature at the rear of the barrel | 250 to 280 °C | ||
| Exhaust hole depth | 0.038 to 0.076 mm | ||
| Temperature at the front of the material cylinder | 255 to 290 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 75 to 100 °C | ||
| Spray nozzle temperature | 260 to 290 °C |