TPEE BEXLOY® 5526 DUPONT TAIWAN

Unit Price:US$ 9,590 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Kaoshiung port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Transaction Guarantee:

Supplier Information

Dongguan Lianzhan Plastic Co., Ltd.

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜High mobility｜UV resistance｜Weather resistance｜currency
Application Areas:Automotive sector｜Electrical field｜Electronic field｜Electrical appliances｜Fitness equipment
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ISO 8256/1	270	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
	UL flame retardant rating	3.0mm	UL 94	HB
		UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	3.0mm	IEC 60695-11-10,-20	HB
Extreme Oxygen Index		ISO 4589-2	21	%
FMVSS flammability		FMVSS302	SE/B
Fogging-G-value	condensate	ISO 6452	1E-04	g
Burning rate	1.00mm	ISO 3795	28	mm/min
elastomer	Test Condition	Test Method	Test Result	Test Unit
tear strength	Flow	ISO 34-1	130	kN/m
tear strength	tear strength	横向Flow	ISO 34-1	130	kN/m
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield	ISO 527-2	15.0	Mpa
	tensile strength	Break	ISO 527-2	40.0	Mpa
	tensile strength	tensile strength	5.0%Strain	ISO 527-2	6.90	Mpa
Tensile modulus		ISO 527-2	190	Mpa
tensile strength	10%Strain	ISO 527-2	11.0	Mpa
tensile strength	tensile strength	50%Strain	ISO 527-2	14.0	Mpa
Tensile strain	Yield	ISO 527-2	35	%
Tensile strain	Tensile strain	Break	ISO 527-2	>300	%
Nominal tensile fracture strain		ISO 527-2	780	%
Tensile creep modulus	1hr	ISO 899-1	170	Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	130	Mpa
Bending modulus		ISO 178	200	Mpa
Wear resistance		ISO 4649	120	mm³
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD：EffectiveThermalDiffusivity	ISO 11359-2	9E-08	m²/s
	Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	1.7E-04	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：--	ISO 11359-2	2E-04	cm/cm/°C
Brittle temperature		ISO 974	-98.0	°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	65.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	45.0	°C
Glass transition temperature		ISO 11357-2	-20.0	°C
Vicat softening temperature	--	ISO 306/A50	180	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	75.0	°C
Melting temperature		ISO 11357-3	203	°C
Linear coefficient of thermal expansion	MD：--	ISO 11359-2	2E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	1.8E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.20	%
	Water absorption rate	Saturation,23°C,2.00mm	ISO 62	0.60	%
	Water absorption rate	Water absorption rate	23°C,24hr	ISO 62	0.60	%
Shrinkage rate	MD	ISO 294-4	1.4	%
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	1.4	%
Melt Volume Flow Rate (MVR)	220°C/2.16kg	ISO 1133	17.5	cm3/10min
melt mass-flow rate		ISO 1133	18	g/10min
MediumDensity			1.04	g/cm³
SpecificHeatCapacity of Melt			2110	J/kg/°C
ThermalConductivityofMelt			0.19	W/m/K
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	1MHz	IEC 60250	0.038
Dissipation factor	Dissipation factor	100Hz	IEC 60250	9E-03
Relative permittivity	1MHz	IEC 60250	4.60
Relative permittivity	Relative permittivity	100Hz	IEC 60250	4.90
Dielectric strength		IEC 60243-1	20	KV/mm
Volume resistivity		IEC 60093	4E+13	ohms·cm
Surface resistivity		IEC 60093	>1.0E+15	ohms
Compared to the anti leakage trace index		IEC 60112	PLC 0
hardness	Test Condition	Test Method	Test Result	Test Unit
Shore hardness	ShoreD	ISO 868	55
Shore hardness	Shore hardness	ShoreD,15Sec	ISO 868	51
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Odor		VDA270	5.00

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
ASIAPLAS	US$ 8060 /MT
Guangdong Jushang	US$ 9070 /MT
Shanghai Huibao/Huibai	US$ 9200 /MT
Dongguan Sharp Plastic	US$ 9260 /MT
Shenzhen Jiuhe	US$ 9650 /MT

Supplier Join

Get App

Top

TPEE BEXLOY® 5526 DUPONT TAIWAN

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index