PA6 LNP™ THERMOCOMP™ PX13012-BKNAT SABIC INNOVATIVE NETHERLANDS
138
- Unit Price:US$ 2,850 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Dimensional stability｜Low Specific Gravity｜Filler: Mineral filler
- Application Areas:Automotive body panels｜Automotive sector
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flow direction: 24 hours | ISO 294-4 | 0.55 % | |
| Water absorption rate | ISO 62 | 0.23 % | |
| flow | 内部方法 | 0.70 % | |
| Flow: 24 hours | ASTM D955 | 0.55 % | |
| Lateral flow: 24 hours | ASTM D955 | 0.65 % | |
| Vertical flow direction: 24 hours | ISO 294-4 | 0.65 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| Burning wire flammability index | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | IEC 60695-2-13 | 750 °C | |
| IEC 60695-2-13 | 775 °C | ||
| IEC 60695-2-13 | 800 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| --2 | ASTM D638 | 10400 Mpa | |
| yield | ASTM D638 | 68.0 Mpa | |
| fracture | ISO 527-2/5 | 75.0 Mpa | |
| ASTM D638 | 1.2 % | ||
| ISO 527-2/5 | 1.1 % | ||
| 50.0mm span | ASTM D790 | 11800 Mpa | |
| --6 | ISO 178 | 12000 Mpa | |
| --7 | ISO 178 | 105 Mpa | |
| Fracture, 50.0mm span | ASTM D790 | 119 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 23°C | ASTM D256 | 15 J/m | |
| ISO 180/1A | 3.0 kJ/m² | ||
| ASTM D4812 | 150 J/m | ||
| ISO 180/1U | 9.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V | |
| High arc combustion index (HAI) | UL 746 | PLC 0 | |
| Hot wire ignition (HWI) | UL 746 | PLC 0 | |
| Surface Resistivity | ASTM D257 | 4E+14 ohms | |
| dielectric strength | ASTM D149 | 7.2 KV/mm | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | IEC 60695-10-2 | Pass | |
| Flow: -40 to 40 ° C | ASTME831 | 3.3E-05 cm/cm/°C | |
| Flow: -30 to 80 ° C | ISO 11359-2 | 3.9E-05 cm/cm/°C | |
| Horizontal: -40 to 40 ° C | ASTME831 | 4.4E-05 cm/cm/°C | |
| Horizontal: -30 to 80 ° C | ISO 11359-2 | 5.5E-05 cm/cm/°C | |
| thermal conductivity | ISO 22007-2 | 1.2 W/m/K | |
| ISO 22007-2 | 5.5 W/m/K | ||
| 0.45MPa, Unanealed, 3.20mm | ASTM D648 | 203 °C | |
| 0.45MPa, Unanealed, 64.0mm span | ISO 75-2/Bf | 203 °C | |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 137 °C | |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 160 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.