PA6 PX13012-BKNAT SABIC INNOVATIVE NETHERLANDS
LNP™ THERMOCOMP™
Automotive body panels、Automotive sector
Dimensional stability、Low Specific Gravity、Filler: Mineral filler
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/PX13012-BKNAT |
|---|---|---|---|
| 23°C | ISO 180/1A | 3.0 kJ/m² | |
| ISO 180/1U | 9.0 kJ/m² | ||
| ASTM D256 | 15 J/m | ||
| ASTM D4812 | 150 J/m |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/PX13012-BKNAT |
|---|---|---|---|
| dielectric strength | 1.60mm,inOil | ASTM D149 | 7.2 KV/mm |
| Surface Resistivity | ASTM D257 | 4E+14 ohms | |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 0 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| IEC 60112 | V |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/PX13012-BKNAT |
|---|---|---|---|
| --2 | ASTM D638 | 10400 Mpa | |
| yield | ASTM D638 | 68.0 Mpa | |
| fracture | ISO 527-2/5 | 75.0 Mpa | |
| ASTM D638 | 1.2 % | ||
| --6 | ISO 178 | 12000 Mpa | |
| 50.0mm span | ASTM D790 | 11800 Mpa | |
| fracture | ISO 527-2/5 | 1.1 % | |
| --7 | ISO 178 | 105 Mpa | |
| Fracture, 50.0mm span | ASTM D790 | 119 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/PX13012-BKNAT |
|---|---|---|---|
| Burning wire flammability index | 0.800mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 0.800mm | IEC 60695-2-13 | 750 °C |
| UL flame retardant rating | 0.800mm | UL 94 | V-0 |
| Hot filament ignition temperature | 3.00mm | IEC 60695-2-13 | 800 °C |
| 1.60mm | IEC 60695-2-13 | 775 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/PX13012-BKNAT |
|---|---|---|---|
| Vertical flow direction: 24 hours | 垂直方向, 24小时 | ISO 294-4 | 0.65 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.23 % |
| Flow: 24 hours | 24小时 | ASTM D955 | 0.55 % |
| Lateral flow: 24 hours | 横向, 24小时 | ASTM D955 | 0.65 % |
| Flow direction: 24 hours | 流动方向, 24小时 | ISO 294-4 | 0.55 % |
| flow | 内部方法 | 0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/PX13012-BKNAT |
|---|---|---|---|
| thermal conductivity | --13 | ISO 22007-2 | 1.2 W/m/K |
| Flow: -30 to 80 ° C | ISO 11359-2 | 3.9E-05 cm/cm/°C | |
| Flow: -40 to 40 ° C | ASTME831 | 3.3E-05 cm/cm/°C | |
| ball-indentation hardness | 165°C | IEC 60695-10-2 | Pass |
| Horizontal: -40 to 40 ° C | 横向, -40到40℃ | ASTME831 | 4.4E-05 cm/cm/°C |
| Horizontal: -30 to 80 ° C | ISO 11359-2 | 5.5E-05 cm/cm/°C | |
| thermal conductivity | --14 | ISO 22007-2 | 5.5 W/m/K |
| 0.45MPa, Unanealed, 64.0mm span | ISO 75-2/Bf | 203 °C | |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 160 °C | |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 137 °C | |
| 0.45MPa, Unanealed, 3.20mm | ASTM D648 | 203 °C |