Material Description
- Material Properties:Thermal stability｜Glass fiber reinforced｜purpose｜Mechanical components｜Engineering parts｜Industrial applications｜Automotive Applications
- Application Areas:Automotive sector｜Bottle cap｜sporting goods｜Electronic field｜Electrical field
- Color:--
- Grade:Enhanced level
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 258 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 238 °C | |
| melting temperature | ISO 11357-3 | 262 °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO 11359-2 | 4E-05 cm/cm/°C |
| MD：-40to23°C | ISO 11359-2 | 4.2E-05 cm/cm/°C | |
| MD：55to160°C | ISO 11359-2 | 2.6E-05 cm/cm/°C | |
| TD：-- | ISO 11359-2 | 9.3E-05 cm/cm/°C | |
| TD：-40to23°C | ISO 11359-2 | 7.7E-05 cm/cm/°C | |
| TD：55to160°C | ISO 11359-2 | 1.5E-04 cm/cm/°C | |
| Combustibility (rate) | UL 94 | HB | |
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 258 ℃（℉） |
| HDT | ASTM D648/ISO 75 | 238 ℃（℉） | |
| melting temperature | 262 ℃（℉） | ||
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 0.77 mm/mm.℃ |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | PA66.13％玻纤增强.热稳定.注塑树脂 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | 1.00mm | ISO 3795 | 26 mm/min |
| UL flame retardant rating | 0.71mm | UL 94 | HB |
| 1.5mm | UL 94 | HB | |
| 0.71mm | IEC 60695-11-10,-20 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| FMVSS flammability | FMVSS302 | B |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Emissions of Organic Compounds | VDA277 | 6.00 µgC/g |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | TD | ISO 294-4 | 1.0 % |
| MD | ISO 294-4 | 0.50 % | |
| Ejection Temperature | 210 °C | ||
| density | ASTM D792/ISO 1183 | 1.23 | |
| shrinkage rate | ASTM D955 | 0.7-1.2 % | |
| Water absorption rate | ASTM D570/ISO 62 | 2.2 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ISO 178 | 190 Mpa | |
| Tensile modulus | ISO 527-2 | 5500 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 120 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.7 % |
| flexural modulus | ISO 178 | 4900 Mpa | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 5 kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 4.5 (-40℃) kg·cm/cm(J/M)ft·lb/in | ||
| Elongation at break | ASTM D638/ISO 527 | 2.7 % | |
| Tensile modulus | ASTM D638/ISO 527 | 5500 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 120 kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | ASTM D790/ISO 178 | 4900 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 190 kg·cm/cm(J/M)ft·lb/in |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.