Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 70G13HS1L BK031 DUPONT USA
Zytel®
Automotive sector,Bottle cap,sporting goods,Electronic field,Electrical field
Thermal stability,Glass fiber reinforced,purpose,Mechanical components,Engineering parts,Industrial applications,Automotive Applications
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | DUPONT USA/70G13HS1L BK031 |
|---|---|---|---|
| Emissions of Organic Compounds | VDA277 | 6.00 µgC/g |
| thermal performance | Test Condition | Test Method | DUPONT USA/70G13HS1L BK031 |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 258 °C |
| Linear coefficient of thermal expansion | MD：-- | ISO 11359-2 | 4E-05 cm/cm/°C |
| MD：55to160°C | ISO 11359-2 | 2.6E-05 cm/cm/°C | |
| ASTM D696/ISO 11359 | 0.77 mm/mm.℃ | ||
| melting temperature | ISO 11357-3 | 262 °C | |
| 262 ℃（℉） | |||
| Heat Deflection Temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 238 °C |
| Linear coefficient of thermal expansion | TD：-40to23°C | ISO 11359-2 | 7.7E-05 cm/cm/°C |
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 238 ℃（℉） |
| Linear coefficient of thermal expansion | MD：-40to23°C | ISO 11359-2 | 4.2E-05 cm/cm/°C |
| Combustibility (rate) | UL 94 | HB | |
| Linear coefficient of thermal expansion | TD：-- | ISO 11359-2 | 9.3E-05 cm/cm/°C |
| TD：55to160°C | ISO 11359-2 | 1.5E-04 cm/cm/°C |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/70G13HS1L BK031 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 4.5 (-40℃) kg·cm/cm(J/M)ft·lb/in | |
| Tensile modulus | ISO 527-2 | 5500 Mpa | |
| Elongation at break | ASTM D638/ISO 527 | 2.7 % | |
| bending strength | ISO 178 | 190 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 120 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.7 % |
| tensile strength | ASTM D638/ISO 527 | 120 kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | ISO 178 | 4900 Mpa | |
| Tensile modulus | ASTM D638/ISO 527 | 5500 kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | ASTM D790/ISO 178 | 4900 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 190 kg·cm/cm(J/M)ft·lb/in |
| other | Test Condition | Test Method | DUPONT USA/70G13HS1L BK031 |
|---|---|---|---|
| characteristic | PA66.13％玻纤增强.热稳定.注塑树脂 |
| Physical properties | Test Condition | Test Method | DUPONT USA/70G13HS1L BK031 |
|---|---|---|---|
| shrinkage rate | ASTM D955 | 0.7-1.2 % | |
| density | ASTM D792/ISO 1183 | 1.23 | |
| shrinkage rate | TD | ISO 294-4 | 1.0 % |
| Ejection Temperature | 210 °C | ||
| shrinkage rate | MD | ISO 294-4 | 0.50 % |
| Water absorption rate | ASTM D570/ISO 62 | 2.2 % |
| flammability | Test Condition | Test Method | DUPONT USA/70G13HS1L BK031 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | HB |
| FMVSS flammability | FMVSS302 | B | |
| UL flame retardant rating | 0.71mm | IEC 60695-11-10,-20 | HB |
| 1.5mm | UL 94 | HB | |
| burning rate | 1.00mm | ISO 3795 | 26 mm/min |
| UL flame retardant rating | 0.71mm | UL 94 | HB |