LDPE LD2420H PCC IRAN
261
- Unit Price:US$ 1,597 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:159.5MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Low speed solidification point｜Low speed solidification point｜optical performance ｜Good processability｜No additives｜General purpose
- Application Areas:Food packaging｜Foam｜chip｜film｜Foam｜Food packaging｜Shrinkable film｜General purpose
- Color:--
- Grade:--
Technical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Vicat softening temperature | ASTM D1525 | 93.0 °C | |
| Melting temperature | ISO 11357-3 | 111 °C |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | 20°, 50.0 μm, Blown Film | ASTM D2457 | > 80 |
| turbidity | 50.0 μm, Blown Film | ASTM D1003 | < 8.0 % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 190℃/2.16 kg | ISO 1133 | 1.9 g/10 min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | Compression Molded | ISO 527-2 | 260 Mpa |
| tensile strength | Yield, Compression Molded | ISO 527-2 | 11.0 Mpa |
| Film thickness - tested | 50 µm | ||
| tensile strength | MD: Break, 50 μm, Blown Film | ISO 527-3 | 21.0 Mpa |
| TD: Break, 50 μm, Blown Film | ISO 527-3 | 20.0 Mpa | |
| elongation | MD: Break, 50 μm, Blown Film | ISO 527-3 | 250 % |
| TD: Break, 50 μm, Blown Film | ISO 527-3 | 600 % | |
| Dart impact | 50 μm, Blown Film | ASTM D1709 | 90 g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.