LDPE LD2420H PCC IRAN
--
Food packaging、Foam、chip、film、Foam、Food packaging、Shrinkable film、General purpose
Low speed solidification 、Low speed solidification 、optical performance 、Good processability、No additives、General purpose
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | PCC IRAN/LD2420H |
|---|---|---|---|
| Tensile stress | 屈服, 模压成型 | ISO 527-2 | 11.0 Mpa |
| elongation | MD: 断裂, 50 µm, 吹塑薄膜 | ISO 527-3 | 250 % |
| TD: 断裂, 50 µm, 吹塑薄膜 | ISO 527-3 | 600 % | |
| Tensile stress | TD: 断裂, 50 µm, 吹塑薄膜 | ISO 527-3 | 20.0 Mpa |
| Film thickness - tested | 50 µm | ||
| Tensile stress | MD: 断裂, 50 µm, 吹塑薄膜 | ISO 527-3 | 21.0 Mpa |
| Falling hammer impact | 50 µm, 吹塑薄膜 | ASTM D1709 | 90 g |
| Tensile modulus | 模压成型 | ISO 527-2 | 260 Mpa |
| optical performance | Test Condition | Test Method | PCC IRAN/LD2420H |
|---|---|---|---|
| Haze ratio | 50.0 µm, 吹塑薄膜 | ASTM D1003 | < 8.0 % |
| gloss | 20°, 50.0 µm, 吹塑薄膜 | ASTM D2457 | > 80 |
| physical property | Test Condition | Test Method | PCC IRAN/LD2420H |
|---|---|---|---|
| melt mass-flow rate | 190℃/2.16 kg | ISO 1133 | 1.9 g/10 min |
| Thermal performance | Test Condition | Test Method | PCC IRAN/LD2420H |
|---|---|---|---|
| vicat | ASTM D1525 | 93.0 °C | |
| melting temperature | ISO 11357-3 | 111 °C |