PC LEXAN™ EXL4419-BR6G123 SABIC INNOVATIVE NANSHA

170

Unit Price:US$ 5,138 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
26MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:enhance｜Glass fiber reinforced｜Low temperature resistance
Application Areas:Automotive sector｜Electrical appliances｜Electronic field｜Electrical field｜Automotive interior parts｜Automotive External Parts
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	15 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	25 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Dart impact	23°C, Total Energy	ASTM D3763	40.0 J

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--2	ASTM D638	3300 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	3300 Mpa
tensile strength	Yield3	ASTM D638	53.0 Mpa
	tensile strength	Yield	ISO 527-2/5	55.0 Mpa
		tensile strength	Break3	ASTM D638	44.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/5	43.0 Mpa
elongation	Yield3	ASTM D638	4.5 %
	elongation	Yield	ISO 527-2/5	4.5 %
		elongation	Break3	ASTM D638	20 %
		elongation	elongation	Break	ISO 527-2/5	13 %
Bending modulus	50.0 mm Span4	ASTM D790	3200 Mpa
Bending modulus	Bending modulus	--5	ISO 178	3300 Mpa
bending strength	--5,6	ISO 178	90.0 Mpa
bending strength	bending strength	Yield, 50.0 mm Span4	ASTM D790	95.0 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			120 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			40 to 60 %
Temperature at the rear of the barrel			290 to 310 °C
Temperature in the middle of the barrel			300 to 320 °C
Temperature at the front of the material cylinder			310 to 330 °C
Spray nozzle temperature			305 to 325 °C
Processing (melt) temperature			310 to 330 °C
Mold temperature			80 to 115 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 70 rpm
Exhaust hole depth			0.025 to 0.076 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	135 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Af	134 °C
Vicat softening temperature	--	ASTM D152510	145 °C
	Vicat softening temperature	--	ISO 306/B50	144 °C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	146 °C
Ball Pressure Test	73 to 77°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	4.1E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	6.9E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	6.9E-5 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	11 g/10 min
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	10.0 cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.20 - 0.60 %
Water absorption rate	Saturation, 23°C	ISO 62	0.12 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.46 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		ASTM D257	2.9E+17 ohms
Volume resistivity		ASTM D257	1.8E+17 ohms·cm
Dielectric strength	1.60 mm, in Oil	ASTM D149	32 KV/mm
Dielectric constant	1 MHz	ASTM D150	3.04
Dielectric constant	Dielectric constant	1.90 GHz	Internal Method	2.95
Dissipation factor	1 MHz	ASTM D150	8.6E-3
Dissipation factor	Dissipation factor	1.90 GHz	Internal Method	5.7E-3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC LEXAN™ EXL4419-BR6G123 SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet Compare

Technical Data Sheet