PA/MXD6

PA/MXD6 RENY™ N-252A MITSUBISHI ENGINEERING JAPAN

380

Unit Price:US$ 4,787 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
26MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact｜High rigidity｜Filler: Glass mineral｜25% filler by weight
Application Areas:Electronic and electrical accessories｜Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179	31 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	25700 Mpa
tensile strength	Break	ISO 527-2	174 Mpa
Tensile strain	Break	ISO 527-2	11 %
Bending modulus		ISO 178	21900 Mpa
bending strength		ISO 178	289 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	236 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	227 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	2E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	4E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	275°C/2.16kg	ISO 1133	2.6 g/10min
Melt Volume Flow Rate (MVR)	275°C/2.16kg	ISO 1133	1.90 cm3/10min
Shrinkage rate			0.45 %
Water absorption rate	Saturation,23°C	ISO 62	0.24 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.1 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 60093	6E+15 ohms·cm
Dielectric strength	1.00mm	IEC 60243-1	21 KV/mm
Relative permittivity	100Hz	IEC 60250	5.00
Relative permittivity	Relative permittivity	1MHz	IEC 60250	5.00
Dissipation factor	100Hz	IEC 60250	0.011
Dissipation factor	Dissipation factor	1MHz	IEC 60250	8E-03
Compared to the anti leakage trace index		IEC 60112	V
Surface resistivity		IEC 60093	4E+15 ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.