PA/MXD6 N-252A MITSUBISHI ENGINEERING JAPAN
RENY™ 
Electronic and electrical accessories,Automotive sector
High impact,High rigidity,Filler: Glass mineral,25% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

thermal performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/N-252A
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B236 °C
1.8MPa,UnannealedISO 75-2/A227 °C
Linear coefficient of thermal expansionTDISO 11359-24E-05 cm/cm/°C
MDISO 11359-22E-05 cm/cm/°C
mechanical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/N-252A
Bending modulusISO 17821900 Mpa
bending strengthISO 178289 Mpa
Tensile modulusISO 527-225700 Mpa
Tensile strainBreakISO 527-211 %
tensile strengthBreakISO 527-2174 Mpa
Electrical performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/N-252A
Compared to the anti leakage trace indexIEC 60112 V
Dielectric strength1.00mmIEC 60243-121 KV/mm
Dissipation factor1MHzIEC 602508E-03
100HzIEC 602500.011
Relative permittivity100HzIEC 602505.00
1MHzIEC 602505.00
Surface resistivityIEC 600934E+15 ohms
Volume resistivityIEC 600936E+15 ohms·cm
Physical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/N-252A
melt mass-flow rate275°C/2.16kgISO 11332.6 g/10min
Melt Volume Flow Rate (MVR)275°C/2.16kgISO 11331.90 cm3/10min
Shrinkage rate0.45 %
Water absorption rateEquilibrium,23°C,50%RHISO 621.1 %
Saturation,23°CISO 620.24 %
impact performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/N-252A
Impact strength of simply supported beam without notch23°CISO 17931 kJ/m²
flammabilityTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/N-252A
UL flame retardant rating1.6mmUL 94HB