Material Description
- Material Properties:transparent｜stability
- Application Areas:toothbrush｜Household daily necessities｜Monitor｜electrical equipment
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Disassembly rate | 1.569 | ||
| Shrinkage rate | 0.3-0.7 % | ||
| Melting temperature range for pipeline extrusion | 220-240 °C | ||
| Water absorption rate | 0.2 % | ||
| melt mass-flow rate | 12 | ||
| 10 | |||
| Melting temperature range for injection molding | 220-270 °C | ||
| Mold temperature range | 40-80 °C |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 通用级别 | ||
| purpose | 制笔 浴室器具 化妆品容器 盛具 牙刷手柄 拨号盘 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 83 | |
| Charpy Notched Impact Strength | 2 KJ/m | ||
| Rockwell hardness | 83 M | ||
| Impact strength of cantilever beam gap | 2 KJ/m | ||
| ball-indentation hardness | 165 Mpa | ||
| Breaking stress | 75 Mpa | ||
| Tensile stress | 125 Mpa | ||
| elongation | 3 % | ||
| Tensile modulus | 3800 Mpa | ||
| Charpy Notched Impact Strength | 18/18 KJ/m | ||
| Tensile creep modulus | 2800 Mpa |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 10.8 kg·cm/cm(J/M)ft·lb/in | |
| Shrinkage rate | ASTM D955 | 0.3-0.7 % | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 12 g/10min | |
| ASTM D1238/ISO 1133 | 10 g/10min | ||
| Water absorption rate | ASTM D570/ISO 62 | 0.2 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Relative Arc Track Index CTI Test Solution | CTI 425 | ||
| dielectric constant | 3/2.7 | ||
| Volume resistivity | 10 Ω.cm | ||
| Surface Resistivity | 10 Ω | ||
| Relative Arc Track Index CTI Test Solution | CTI 200M | ||
| dielectric strength | 95 KV/mm | ||
| loss angle | 0.004/0.007 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | 85 ℃（℉） | ||
| vicat | ASTM D1525/ISO R306 | 106 ℃（℉） | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 7 mm/mm.℃ | |
| Heat distortion temperature | 102 °C | ||
| maximum service temperature | 85 °C | ||
| Heat distortion temperature | 98 °C | ||
| Conductivity | 0.17 W/K.m | ||
| Linear coefficient of thermal expansion | 7 | ||
| vicat | 106 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.