ABS CYCOLAC™  MG47-BK4500 SABIC INNOVATIVE US

309
  • Unit Price:US$ 1,951 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    30MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High toughness｜Low temperature resistance｜High impact resistance｜High gloss
  • Application Areas:small home appliances
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°CISO 179/1eA9.0 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA26 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A8.0 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A22 kJ/m²
Dart impact23°C,TotalEnergyASTM D376330.0 J
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.5mmUL 94HB
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulusASTM D6382270 Mpa
Tensile modulusISO 527-2/12370 Mpa
tensile strengthYieldASTM D63844.0 Mpa
tensile strengthYieldISO 527-2/5047.0 Mpa
tensile strengthBreakASTM D63833.0 Mpa
tensile strengthBreakISO 527-2/5035.0 Mpa
elongationYieldASTM D6382.0 %
Tensile strainYieldISO 527-2/502.6 %
elongationBreakASTM D63824 %
Tensile strainBreakISO 527-2/5025 %
Bending modulus50.0mmSpanASTM D7902300 Mpa
Bending modulusISO 1782200 Mpa
bending strengthISO 17870.0 Mpa
bending strengthYield,50.0mmSpanASTM D79070.0 Mpa
thermal performanceTest ConditionTest MethodTest Result
Vicat softening temperature--ISO 306/B5098.0 °C
Vicat softening temperature--ISO 306/B120100 °C
Linear coefficient of thermal expansionMD：-40to40°CASTME8318.8E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CASTME8318.8E-05 cm/cm/°C
RTI ElecUL 74660.0 °C
RTI ImpUL 74660.0 °C
RTI StrUL 74660.0 °C
Hot deformation temperature0.45MPa,Unannealed,3.20mmASTM D64894.0 °C
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D64880.0 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af81.0 °C
Vicat softening temperatureASTM D15251099.0 °C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate230°C/3.8kgASTM D12385.6 g/10min
melt mass-flow rate220°C/10.0kgISO 113318 g/10min
Shrinkage rateMD：3.20mmInternal Method0.50-0.80 %
Melt viscosity240°C,1000sec^-1ASTM D3835225 Pa·s
Electrical performanceTest ConditionTest MethodTest Result
High voltage arc tracing rateHVTRUL 746PLC 3
Hot wire ignitionHWIUL 746PLC 3
Arc resistanceASTM D495PLC6
Compared to the anti leakage trace indexCTIUL 746PLC 0
High arc combustion indexHAIUL 746PLC 0
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-ScaleASTM D785112
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.