Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS MG47-BK4500 SABIC INNOVATIVE US
CYCOLAC™
small home appliances
High toughness、Low temperature resistanc、High impact resistance、High gloss
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/MG47-BK4500 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 26 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 30.0 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 9.0 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 8.0 kJ/m² |
| 23°C | ISO 180/1A | 22 kJ/m² |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/MG47-BK4500 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 112 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/MG47-BK4500 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2370 Mpa | |
| elongation | 屈服 | ASTM D638 | 2.0 % |
| tensile strength | 断裂 | ASTM D638 | 33.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 2.6 % |
| tensile strength | 断裂 | ISO 527-2/50 | 35.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2300 Mpa |
| Tensile modulus | ASTM D638 | 2270 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 47.0 Mpa |
| elongation | 断裂 | ASTM D638 | 24 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 70.0 Mpa |
| ISO 178 | 70.0 Mpa | ||
| Flexural modulus | ISO 178 | 2200 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 44.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 25 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/MG47-BK4500 |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 3 |
| arc resistance | ASTM D495 | PLC6 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/MG47-BK4500 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/MG47-BK4500 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.80 % |
| melt viscosity | 240°C,1000sec^-1 | ASTM D3835 | 225 Pa·s |
| melt mass-flow rate | 230°C/3.8kg | ASTM D1238 | 5.6 g/10min |
| 220°C/10.0kg | ISO 1133 | 18 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/MG47-BK4500 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 100 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 8.8E-05 cm/cm/°C |
| vicat | -- | ISO 306/B50 | 98.0 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 8.8E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 94.0 °C |
| RTI Imp | UL 746 | 60.0 °C | |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 81.0 °C |
| vicat | ASTM D152510 | 99.0 °C | |
| RTI Str | UL 746 | 60.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 80.0 °C |
| RTI Elec | UL 746 | 60.0 °C |