PA66 Zytel® FR52G20LX DUPONT USA
138
- Unit Price:US$ 4,190 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:46.3MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Thermal stability｜Filler: Glass fiber reinforced material｜20% filler by weight
- Application Areas:Automotive components｜Home appliance components
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | °C | 310 -- | |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 2.5E-05 -- |
| MD:-40到23°C | cm/cm/°C | 2.7E-05 -- | |
| MD:55到160°C | cm/cm/°C | 2.1E-05 -- | |
| TD | cm/cm/°C | 6.8E-05 -- | |
| TD:-40到23°C | cm/cm/°C | 6.4E-05 -- | |
| TD:55到160°C | cm/cm/°C | 1E-04 -- | |
| Heat Deflection Temperature | 1.8MPa,未退火 | °C | 276 -- |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flammability level | 0.750mm | V-0 -- | |
| 1.50mm | V-0 -- | ||
| Burning wire flammability index | 0.400mm | °C | 960 -- |
| Hot filament ignition temperature | 0.400mm | °C | 725 -- |
| Limiting Oxygen Index | % | 35 -- |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | kJ/m² | 40 |
| 23°C | kJ/m² | 40 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | TD | % | 1.1 -- |
| MD | % | 0.30 -- |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | ohms·cm | >1.0E+15 -- | |
| dielectric strength | kV/mm | 42 -- | |
| Compared to the Leakage Tracking Index (CTI) | V | -- |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | 8200 MPa | ||
| tensile strength | 断裂 | 135 MPa | |
| Tensile strain | 断裂 | % | 2.4 2.2 |
| flexural modulus | MPa | 7800 8200 | |
| bending strength | MPa | 215 180 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.