Material Description
- Material Properties:High hardness｜Glass fiber reinforced
- Application Areas:Automotive Applications
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 190 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/A | 163 °C | |
| melting temperature | ISO 11357-3 | 168 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 4.0E-5 cm/cm/°C | |
| maximum service temperature | 110 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flammability level | UL 94 | HB | |
| ISO Type | ISO 6383-1 | POM-K. M-GNR. 02-003. GF25 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 60 kJ/m² | |
| ISO 179/1eU | 55 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | ISO 1133 | 4.00 cm3/10min | |
| shrinkage rate | ISO 294-4 | 1.4 % | |
| ISO 294-4 | 0.70 % | ||
| Water absorption rate | ISO 62 | 0.90 % | |
| ISO 62 | 0.15 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1.0E+14 ohms | |
| volume resistivity | IEC 60093 | 1.0E+14 ohms·cm | |
| dielectric strength | IEC 60243-1 | 85 KV/mm | |
| relative permittivity | IEC 60250 | 4.00 | |
| Dissipation Factor | IEC 60250 | 7.0E-3 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 100 °C | ||
| drying time | 3.0 hr | ||
| Suggested maximum moisture content | 0.20 % | ||
| Hopper temperature | 200 °C | ||
| Temperature at the rear of the barrel | 205 °C | ||
| Temperature in the middle of the barrel | 205 °C | ||
| Temperature at the front of the material cylinder | 210 °C | ||
| Spray nozzle temperature | 210 °C | ||
| Processing (melt) temperature | 190 to 230 °C | ||
| mold temperature | 60 to 120 °C | ||
| Residence Time | < 10.0 min | ||
| screw speed | < 18 m/min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 8800 Mpa | |
| tensile strength | ISO 527-2 | 130 Mpa | |
| Tensile strain | ISO 527-2 | 3.0 % | |
| Tensile creep modulus | ISO 899-1 | 5800 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.