Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM N2200G53 BASF KOREA
Ultraform®
Automotive Applications
High hardness,Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF KOREA/N2200G53 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 55 kJ/m² |
| -30°C | ISO 179/1eU | 60 kJ/m² |
| hardness | Test Condition | Test Method | BASF KOREA/N2200G53 |
|---|---|---|---|
| ball-indentation hardness | H 961/30 | ISO 2039-1 | 190 Mpa |
| Mechanical properties | Test Condition | Test Method | BASF KOREA/N2200G53 |
|---|---|---|---|
| Tensile creep modulus | 1000 hr | ISO 899-1 | 5800 Mpa |
| Tensile modulus | ISO 527-2 | 8800 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.0 % |
| tensile strength | 断裂 | ISO 527-2 | 130 Mpa |
| Electrical performance | Test Condition | Test Method | BASF KOREA/N2200G53 |
|---|---|---|---|
| Dissipation Factor | 1 MHz | IEC 60250 | 7.0E-3 |
| dielectric strength | IEC 60243-1 | 85 KV/mm | |
| Volume resistivity | IEC 60093 | 1.0E+14 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案 A | IEC 60112 | PLC 0 |
| relative permittivity | 1 MHz | IEC 60250 | 4.00 |
| Surface Resistivity | IEC 60093 | 1.0E+14 ohms |
| flammability | Test Condition | Test Method | BASF KOREA/N2200G53 |
|---|---|---|---|
| Flammability level | UL 94 | HB | |
| ISO Type | ISO 6383-1 | POM-K. M-GNR. 02-003. GF25 |
| physical property | Test Condition | Test Method | BASF KOREA/N2200G53 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.15 % |
| Melt volume flow rate | 190°C/2.16 kg | ISO 1133 | 4.00 cm3/10min |
| Shrinkage rate | 流量 | ISO 294-4 | 0.70 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.90 % |
| Shrinkage rate | 横向流量 | ISO 294-4 | 1.4 % |
| Thermal performance | Test Condition | Test Method | BASF KOREA/N2200G53 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 168 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 163 °C |
| Linear coefficient of thermal expansion | 23 到 55°C，流动 | ISO 11359-2 | 4.0E-5 cm/cm/°C |
| maximum service temperature | 短周期操作 | 110 °C |
| injection | Test Condition | Test Method | BASF KOREA/N2200G53 |
|---|---|---|---|
| drying time | 3.0 hr | ||
| Suggested maximum moisture content | 0.20 % | ||
| Temperature in the middle of the barrel | 205 °C | ||
| Temperature at the rear of the barrel | 205 °C | ||
| Processing (melt) temperature | 190 to 230 °C | ||
| Hopper temperature | 200 °C | ||
| drying temperature | 100 °C | ||
| Temperature at the front of the material cylinder | 210 °C | ||
| screw speed | < 18 m/min | ||
| Temperature | 60 to 120 °C | ||
| Spray nozzle temperature | 210 °C | ||
| Residence Time | < 10.0 min |