PA66

PA66 Vydyne® R533 ASCEND USA

291

Unit Price:US$ 4,939 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
18MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Flame retardant grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180	12 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180	10 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179	80 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179	70 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179	11 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179	10 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75 mm	UL 94	HB
	UL flame retardant rating	1.5 mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	HB
Burning wire flammability index	0.75 mm	IEC 60695-2-12	750 °C
	Burning wire flammability index	1.5 mm	IEC 60695-2-12	725 °C
	Burning wire flammability index	Burning wire flammability index	3.0 mm	IEC 60695-2-12	800 °C
Hot filament ignition temperature	0.75 mm	IEC 60695-2-13	775 °C
	Hot filament ignition temperature	1.5 mm	IEC 60695-2-13	725 °C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	750 °C

mechanical properties	Test Condition	Test Method	Test Result
Poisson's ratio		ISO 527-2	0.40
bending strength	23°C	ISO 178	290 Mpa
Bending modulus	23°C	ISO 178	10200 Mpa
Tensile strain	Break, 23°C	ISO 527-2	3.0 %
tensile strength	Break, 23°C	ISO 527-2	205 Mpa
Tensile modulus	23°C	ISO 527-2	10600 Mpa

injection	Test Condition	Test Method	Test Result
drying time			4.0 hr
Temperature in the middle of the barrel			280 to 310 °C
Suggested maximum material return ratio			50 %
Temperature at the rear of the barrel			280 to 310 °C
drying temperature			80 °C
Temperature at the front of the material cylinder			280 to 310 °C
Spray nozzle temperature			280 to 310 °C
Processing (melt) temperature			285 to 305 °C
Mold temperature			65 to 95 °C

thermal performance	Test Condition	Test Method	Test Result
RTI Elec	3.0 mm	UL 746	120 °C
RTI Imp	0.75 mm	UL 746	100 °C
	RTI Imp	1.5 mm	UL 746	100 °C
	RTI Imp	RTI Imp	3.0 mm	UL 746	105 °C
RTI	0.75 mm	UL 746	125 °C
	RTI	1.5 mm	UL 746	125 °C
	RTI	RTI	3.0 mm	UL 746	125 °C
RTI Elec	1.5 mm	UL 746	120 °C
RTI Elec	RTI Elec	0.75 mm	UL 746	120 °C
Linear coefficient of thermal expansion	Across Flow : 23 to 55°C, 2.00 mm	ISO 11359-2	1.1E-4 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : 23 to 55°C, 2.00 mm	ISO 11359-2	2.1E-5 cm/cm/°C
Melting temperature		ISO 11357-3	260 °C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	250 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	260 °C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.40 g/cm³
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	1.7 %
Water absorption rate	Water absorption rate	24 hr, 23°C	ISO 62	0.80 %
Shrinkage rate	Flow : 23°C, 2.00 mm	ISO 294-4	0.40 %
Shrinkage rate	Shrinkage rate	横向Flow : 23°C, 2.00 mm	ISO 294-4	0.90 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity	3.00 mm	IEC 60093	1.0E+14 ohms·cm
Dielectric strength	1.00 mm	IEC 60243	20 KV/mm
Arc resistance	3.00 mm	ASTM D495	PLC 5
Compared to the anti leakage trace index	3.00 mm	IEC 60112	PLC 0
High arc combustion index	0.75 mm	UL 746	PLC 0
	High arc combustion index	1.5 mm	UL 746	PLC 0
	High arc combustion index	High arc combustion index	3.0 mm	UL 746	PLC 0
High voltage arc tracing rate		UL 746	PLC 1
Hot wire ignition	0.75 mm	UL 746	PLC 4
	Hot wire ignition	1.5 mm	UL 746	PLC 4
	Hot wire ignition	Hot wire ignition	3.0 mm	UL 746	PLC 3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.