TPEE Hytrel® HTR8223 BK320 DUPONT USA
177
- Unit Price:US$ 3,149 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:50MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High temperature resistance｜Chemical resistance
- Application Areas:Automotive Applications｜Cable｜Blow molding applications
- Color:--
- Grade:Withdrawal level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 9.5 g/10min | |
| Melt volume flow rate | ISO 1133 | 10.0 cm3/10min | |
| Shrinkage rate | ISO 294-4 | 1.6 % | |
| ISO 294-4 | 1.6 % | ||
| Water absorption rate | ISO 62 | 0.60 % | |
| ISO 62 | 0.80 % | ||
| ISO 62 | 0.20 % | ||
| MediumDensity | 0.980 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | ISO 868 | 42 | |
| ISO 868 | 38 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | ISO 3795 | <100 mm/min | |
| FMVSS flammability | FMVSS302 | B |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 75.0 Mpa | |
| tensile strength | ISO 527-2 | 26.0 Mpa | |
| ISO 527-2 | 3.50 Mpa | ||
| ISO 527-2 | 5.50 Mpa | ||
| ISO 527-2 | 10.0 Mpa | ||
| ISO 527-2 | 13.0 Mpa | ||
| ISO 527-2 | 19.0 Mpa | ||
| Tensile strain | ISO 527-2 | >300 % | |
| Nominal tensile fracture strain | ISO 527-2 | 680 % | |
| Flexural modulus | ISO 178 | 79.0 Mpa | |
| wear resistance | ISO 4649 | 22.0 mm³ |
| elastomer | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tear strength | ISO 34-1 | 130 kN/m | |
| ISO 34-1 | 120 kN/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 2E+14 ohms | |
| Volume resistivity | IEC 60093 | 9E+12 ohms·cm | |
| dielectric strength | IEC 60243-1 | 18 KV/mm | |
| Dissipation Factor | IEC 60250 | 7E-03 | |
| IEC 60250 | 0.013 | ||
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| brittle temperature | ISO 974 | -100 °C | |
| Glass Transition Temperature | ISO 11357-2 | -50.0 °C | |
| melting temperature | ISO 11357-3 | 195 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 1.7E-04 cm/cm/°C | |
| ISO 11359-2 | 1.7E-04 cm/cm/°C | ||
| Effective thermal diffusivity coefficient | 5.44E-08 m²/s |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.