Material Properties:high strength｜High rigidity｜Glass fiber reinforced｜enhance｜Filler: Glass fiber reinforced material｜35% filler by weight
Application Areas:Automotive sector｜Industrial applications｜Engineering accessories
Color:--
Grade:--

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
melting temperature		DIN EN11357-1	262 °C
Heat Deflection Temperature	0.45MPa,未退火	ISO 75-2/B	265 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,未退火	ISO 75-2/A	250 °C

flammability	Test Condition	Test Method	Test Result
burning rate	1.00mm	FMVSS302	<100 mm/min
UL flame retardant rating	1.6mm	UL 94	HB

Supplementary Information	Test Condition	Test Method	Test Result
ReinforcementContent		ISO 1172	35 %

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	53 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	>50 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Tensile strain	断裂	ISO 527-2/5	2.3 %
flexural modulus		ISO 178	8000 Mpa
bending strength		ISO 178	250 Mpa
Fracture bending strain		ISO 178	3.7 %
Tensile modulus		ISO 527-2/1	11500 Mpa
tensile strength	断裂	ISO 527-2/5	180 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.