PA66 A3GF35 AKRO-PLASTIC GERMANY
AKROMID®
Automotive sector,Industrial applications,Engineering accessories
high strength,High rigidity,Glass fiber reinforced,enhance,Filler: Glass fiber reinf,35% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF35 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | >50 kJ/m² |
| -30°C | ISO 179/1eU | 53 kJ/m² |
| Supplementary Information | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF35 |
|---|---|---|---|
| ReinforcementContent | ISO 1172 | 35 % |
| Mechanical properties | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF35 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 11500 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 180 Mpa |
| bending strength | ISO 178 | 250 Mpa | |
| Flexural modulus | ISO 178 | 8000 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.3 % |
| Fracture bending strain | ISO 178 | 3.7 % |
| flammability | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF35 |
|---|---|---|---|
| burning rate | 1.00mm | FMVSS302 | <100 mm/min |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Thermal performance | Test Condition | Test Method | AKRO-PLASTIC GERMANY/A3GF35 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 265 °C |
| melting temperature | DIN EN11357-1 | 262 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 250 °C |