thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45 MPa, 未退火	ISO 75-2/B	290 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8 MPa, 未退火	ISO 75-2/A	190 °C
melting temperature		ISO 11357-3	295 °C
Linear coefficient of thermal expansion	流动	ISO 11359-2	8.5E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	横向	ISO 11359-2	1.1E-4 cm/cm/°C
Thermal Index - 5000 hr		IEC 60216	152 °C

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	横向流量	ISO 294-4	2.0 %
shrinkage rate	shrinkage rate	流量	ISO 294-4	2.0 %
Water absorption rate	平衡, 23°C, 50% RH	ISO 62	3.2 %

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--	ISO 527-2	3100 Mpa
	Tensile modulus	120°C	ISO 527-2	775 Mpa
		Tensile modulus	160°C	ISO 527-2	650 Mpa
			Tensile modulus	180°C	ISO 527-2	600 Mpa
			Tensile modulus	Tensile modulus	200°C	ISO 527-2	560 Mpa
tensile strength	屈服, 120°C	ISO 527-2	45.0 Mpa
	tensile strength	屈服, 160°C	ISO 527-2	40.0 Mpa
		tensile strength	屈服, 180°C	ISO 527-2	35.0 Mpa
			tensile strength	屈服, 200°C	ISO 527-2	30.0 Mpa
			tensile strength	tensile strength	断裂	ISO 527-2	90.0 Mpa
Tensile strain	断裂	ISO 527-2	20 %
Nominal tensile fracture strain	120°C	ISO 527-2	> 50 %
	Nominal tensile fracture strain	160°C	ISO 527-2	> 50 %
		Nominal tensile fracture strain	180°C	ISO 527-2	> 50 %
		Nominal tensile fracture strain	Nominal tensile fracture strain	200°C	ISO 527-2	> 50 %
flexural modulus		ISO 178	2900 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.