Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA46 HGR2 BK 00001 DSM HOLAND
Stanyl®
Fitness equipment、Home appliance components
Thermal stability、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DSM HOLAND/HGR2 BK 00001 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Mechanical properties | Test Condition | Test Method | DSM HOLAND/HGR2 BK 00001 |
|---|---|---|---|
| Tensile modulus | -- | ISO 527-2 | 3100 Mpa |
| tensile strength | 断裂 | ISO 527-2 | 90.0 Mpa |
| Tensile modulus | 180°C | ISO 527-2 | 600 Mpa |
| 160°C | ISO 527-2 | 650 Mpa | |
| Nominal tensile fracture strain | 200°C | ISO 527-2 | > 50 % |
| Tensile modulus | 120°C | ISO 527-2 | 775 Mpa |
| tensile strength | 屈服, 180°C | ISO 527-2 | 35.0 Mpa |
| 屈服, 160°C | ISO 527-2 | 40.0 Mpa | |
| 屈服, 200°C | ISO 527-2 | 30.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 20 % |
| Flexural modulus | ISO 178 | 2900 Mpa | |
| Tensile modulus | 200°C | ISO 527-2 | 560 Mpa |
| tensile strength | 屈服, 120°C | ISO 527-2 | 45.0 Mpa |
| Nominal tensile fracture strain | 120°C | ISO 527-2 | > 50 % |
| 180°C | ISO 527-2 | > 50 % | |
| 160°C | ISO 527-2 | > 50 % |
| physical property | Test Condition | Test Method | DSM HOLAND/HGR2 BK 00001 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 3.2 % |
| Shrinkage rate | 流量 | ISO 294-4 | 2.0 % |
| 横向流量 | ISO 294-4 | 2.0 % |
| Thermal performance | Test Condition | Test Method | DSM HOLAND/HGR2 BK 00001 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 295 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 290 °C |
| 1.8 MPa, 未退火，HDT | ISO 75-2/A | 190 °C | |
| Thermal Index - 5000 hr | IEC 60216 | 152 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 8.5E-5 cm/cm/°C |
| 横向 | ISO 11359-2 | 1.1E-4 cm/cm/°C |