PA66 Ultramid® A3HG2 BASF GERMANY
203
- Unit Price:US$ 5,318 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:15MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Oil resistant｜Insulation performance｜Glass fiber reinforced
- Application Areas:Electrical components｜machine｜Mechanical components｜Shell
- Color:--
- Grade:Wear resistant grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火 | ASTM D648 | 210 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 210 °C | |
| melting temperature | ASTM D3418 | 260 °C | |
| ISO 3146 | 260 °C | ||
| Linear coefficient of thermal expansion | MD | 3.3E-05 cm/cm/°C | |
| TD | 7.5E-05 cm/cm/°C | ||
| Combustibility (rate) | UL 94 | HB | |
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 210(1.80MPa) ℃（℉） |
| melting temperature | 260 ℃（℉） |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 30 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | IEC 60093 | 1E+13 ohms·cm | |
| dielectric constant | 1MHz | IEC 60250 | 3.50 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.014 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 | |
| volume resistivity | 1.50mm | ASTM D257 | 1E+13 ohms·cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 平衡,50%RH | ASTM D570 | 2.1 % |
| 平衡,23°C,50%RH | ISO 62 | 2.1 % | |
| Melt volume flow rate | 275°C/5.0kg | ISO 1133 | 80.0 cm3/10min |
| shrinkage rate | MD：3.18mm | 0.80 % | |
| Water absorption rate | 饱和 | ASTM D570 | 7.0 % |
| 饱和,23°C | ISO 62 | 7.0 % | |
| density | ASTM D792/ISO 1183 | 1200 | |
| shrinkage rate | ASTM D955 | 0.9 % | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 80 （cm3/10min 275℃/5kg ) g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 6.6-7.3 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | 23°C | ISO 527-2 | 4600 Mpa |
| tensile strength | 断裂,23°C | ASTM D638 | 100 Mpa |
| 断裂,23°C | ISO 527-2 | 100 Mpa | |
| elongation | 断裂,23°C | ASTM D638 | 3.0 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | 3.0 % |
| flexural modulus | 23°C | ASTM D790 | 4480 Mpa |
| 23°C | ISO 178 | 4480 Mpa | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 7 kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 30 kg·cm/cm(J/M)ft·lb/in | ||
| Tensile modulus | ASTM D638/ISO 527 | 4600 kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | ASTM D790/ISO 178 | 4600 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 165 kg·cm/cm(J/M)ft·lb/in | |
| Elongation at break | ASTM D638/ISO 527 | 2.8 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.