Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 A3HG2 BASF GERMANY
Ultramid®
Electrical components,machine,Mechanical components,Shell
Oil resistant,Insulation performance,Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/A3HG2 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 30 kJ/m² |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/A3HG2 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 | |
| Volume resistivity | IEC 60093 | 1E+13 ohms·cm | |
| 1.50mm | ASTM D257 | 1E+13 ohms·cm | |
| dielectric constant | 1MHz | IEC 60250 | 3.50 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.014 |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/A3HG2 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 3.0 % |
| Flexural modulus | 23°C | ISO 178 | 4480 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 4600 Mpa |
| ASTM D638/ISO 527 | 4600 kg/cm²(MPa)[Lb/in²] | ||
| tensile strength | 断裂,23°C | ISO 527-2 | 100 Mpa |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 30 kg·cm/cm(J/M)ft·lb/in | |
| Flexural modulus | ASTM D790/ISO 178 | 4600 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 165 kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 2.8 % | |
| tensile strength | 断裂,23°C | ASTM D638 | 100 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 4480 Mpa |
| elongation | 断裂,23°C | ASTM D638 | 3.0 % |
| Physical properties | Test Condition | Test Method | BASF GERMANY/A3HG2 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.9 % | |
| density | ASTM D792/ISO 1183 | 1200 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 80 （cm3/10min 275℃/5kg ) g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 6.6-7.3 % |
| physical property | Test Condition | Test Method | BASF GERMANY/A3HG2 |
|---|---|---|---|
| Shrinkage rate | MD：3.18mm | 0.80 % | |
| Water absorption rate | 饱和 | ASTM D570 | 7.0 % |
| 平衡,50%RH | ASTM D570 | 2.1 % | |
| 平衡,23°C,50%RH | ISO 62 | 2.1 % | |
| 饱和,23°C | ISO 62 | 7.0 % | |
| Melt volume flow rate | 275°C/5.0kg | ISO 1133 | 80.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/A3HG2 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 210 °C |
| Combustibility (rate) | UL 94 | HB | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 210(1.80MPa) ℃（℉） |
| Linear coefficient of thermal expansion | MD | 3.3E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 210 °C |
| melting temperature | ASTM D3418 | 260 °C | |
| 260 ℃（℉） | |||
| Linear coefficient of thermal expansion | TD | 7.5E-05 cm/cm/°C | |
| melting temperature | ISO 3146 | 260 °C |