PBT Toraycon® 5201-X10-BK TORAY JAPAN
204
- Unit Price:US$ 2,777 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:33MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant
- Application Areas:Automotive sector｜Electronic field｜Electrical field
- Color:--
- Grade:Impact resistant grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M计秤,23°C | ISO 2039-2 | 70 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 150 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 55.0 °C | |
| Linear coefficient of thermal expansion | MD：-30到100°C | ISO 11359-2 | 1.4E-04 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| BarFlowLength | 250°C,1.00mm | 内部方法 | 8.70 CM |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 290 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | 80×80×3板材 | 2.0-2.5 % | |
| Water absorption rate | 23℃·24小时 | ASTM D-570 | 0.08 % |
| shrinkage rate | TD:3.00mm2 | 内部方法 | 2.5 % |
| MD:3.00mm4 | 内部方法 | 2.0 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.080 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | IEC 60093 | 4E+16 ohms·cm | |
| dielectric strength | IEC 60243-1 | 19 KV/mm | |
| dielectric constant | 23°C,50Hz | IEC 60250 | 3.40 |
| 23°C,1kHz | IEC 60250 | 3.50 | |
| Dissipation Factor | 23°C,50Hz | IEC 60250 | 2E-03 |
| 23°C,1MHz | IEC 60250 | 0.020 | |
| arc resistance | IEC 60950 | 130 sec | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | 23℃ | ASTM D-785 | 59 M标度 |
| tensile strength | 23℃ | ASTM D-638 | 490 kg/cm |
| Impact strength of cantilever beam gap | 无缺口，23℃，1/8时宽 | ASTM D-256 | 不破裂 kg.cm/cm |
| 无缺口，-40℃，1/8时宽 | ASTM D-256 | 160 kg.cm/cm | |
| 缺口，23℃，1/8时宽 | ASTM D-256 | 6.4 kg.cm/cm | |
| flexural modulus | 23°C | ISO 178 | 2400 Mpa |
| bending strength | 23°C | ISO 178 | 80.0 Mpa |
| Impact strength of cantilever beam gap | 缺口，-40℃，1/8时宽 | ASTM D-256 | 5.0 kg.cm/cm |
| flexural modulus | 23℃ | ASTM D-790 | 23 kg/cm |
| bending strength | 23℃ | ASTM D-790 | 770 kg/cm |
| Elongation at break | 23℃ | ASTM D-638 | >150 % |
| Heat Deflection Temperature | 4.6kg/cm | ASTM D-648 | 154 °C |
| 18.6kg.cm | ASTM D-648 | 56 °C | |
| Rockwell hardness | 23℃ | ASTM D-785 | 108 |
| Tensile modulus | 23°C | ISO 527-2 | 2600 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 50.0 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 50 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.