Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 5201-X10-BK TORAY JAPAN
Toraycon®
Automotive sector,Electronic field,Electrical field
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/5201-X10-BK |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 290 kJ/m² |
| hardness | Test Condition | Test Method | TORAY JAPAN/5201-X10-BK |
|---|---|---|---|
| Rockwell hardness | M计秤,23°C | ISO 2039-2 | 70 |
| Supplementary Information | Test Condition | Test Method | TORAY JAPAN/5201-X10-BK |
|---|---|---|---|
| BarFlowLength | 250°C,1.00mm | 内部方法 | 8.70 CM |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/5201-X10-BK |
|---|---|---|---|
| Rockwell hardness | 23℃ | ASTM D-785 | 59 M标度 |
| Impact strength of cantilever beam gap | 无缺口，23℃，1/8时宽 | ASTM D-256 | 不破裂 kg.cm/cm |
| Tensile modulus | 23°C | ISO 527-2 | 2600 Mpa |
| Impact strength of cantilever beam gap | 缺口，-40℃，1/8时宽 | ASTM D-256 | 5.0 kg.cm/cm |
| 缺口，23℃，1/8时宽 | ASTM D-256 | 6.4 kg.cm/cm | |
| Heat distortion temperature | 18.6kg.cm | ASTM D-648 | 56 °C |
| 4.6kg/cm | ASTM D-648 | 154 °C | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 50 % |
| bending strength | 23°C | ISO 178 | 80.0 Mpa |
| 23℃ | ASTM D-790 | 770 kg/cm | |
| elongation at break | 23℃ | ASTM D-638 | >150 % |
| tensile strength | 屈服,23°C | ISO 527-2 | 50.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 2400 Mpa |
| 23℃ | ASTM D-790 | 23 kg/cm | |
| tensile strength | 23℃ | ASTM D-638 | 490 kg/cm |
| Impact strength of cantilever beam gap | 无缺口，-40℃，1/8时宽 | ASTM D-256 | 160 kg.cm/cm |
| Rockwell hardness | 23℃ | ASTM D-785 | 108 |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/5201-X10-BK |
|---|---|---|---|
| dielectric constant | 23°C,50Hz | IEC 60250 | 3.40 |
| 23°C,1kHz | IEC 60250 | 3.50 | |
| dielectric strength | IEC 60243-1 | 19 KV/mm | |
| Volume resistivity | IEC 60093 | 4E+16 ohms·cm | |
| arc resistance | IEC 60950 | 130 sec | |
| Dissipation Factor | 23°C,50Hz | IEC 60250 | 2E-03 |
| 23°C,1MHz | IEC 60250 | 0.020 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| flammability | Test Condition | Test Method | TORAY JAPAN/5201-X10-BK |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| physical property | Test Condition | Test Method | TORAY JAPAN/5201-X10-BK |
|---|---|---|---|
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 2.5 % |
| MD:3.00mm4 | 内部方法 | 2.0 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.080 % |
| 23℃·24小时 | ASTM D-570 | 0.08 % | |
| Shrinkage rate | 80×80×3板材 | 2.0-2.5 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/5201-X10-BK |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 150 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 55.0 °C | |
| Linear coefficient of thermal expansion | MD：-30到100°C | ISO 11359-2 | 1.4E-04 cm/cm/°C |