PA6/66

PA6/66 Ultramid® A3WG6 BK 00546 BASF GERMANY

244

Unit Price:US$ 4,534 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
40MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Enhanced level

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	75 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	90 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	9500 Mpa
tensile strength	Break	ISO 527-2	185 Mpa
Tensile strain	Break	ISO 527-2	3.7 %
Bending modulus		ISO 178	9200 Mpa
bending strength		ISO 178	285 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			80 °C
drying time			4.0 hr
Suggested maximum moisture content			0.15 %
Hopper temperature			80 °C
Temperature at the rear of the barrel			290 °C
Temperature in the middle of the barrel			290 °C
Temperature at the front of the material cylinder			290 °C
Spray nozzle temperature			290 °C
Processing (melt) temperature			280 to 300 °C
Mold temperature			80 to 90 °C
Residence Time			< 10.0 min
Screw speed			< 18 m/min

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	260 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	245 °C
Melting temperature		ISO 11357-3	260 °C
Polymer Abbreviation			PA66-GF30

Physical properties	Test Condition	Test Method	Test Result
Apparent density			0.70 g/cm³
Melt Volume Flow Rate (MVR)	275°C/5.0 kg	ISO 1133	10.0 cm3/10min
Shrinkage rate	横向Flow	ISO 294-4	1.2 %
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	0.40 %
Water absorption rate	Saturation, 23°C	ISO 62	5.6 to 6.3 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	1.5 to 1.9 %
Stickiness	96% H2SO4	ISO 307	160 cm³/g
Mold Shrinkage - Constrained			0.40 to 0.50 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.