PA6/66 A3WG6 BK 00546 BASF GERMANY
Ultramid®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/A3WG6 BK 00546 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 90 kJ/m² |
| -30°C | ISO 179/1eU | 75 kJ/m² |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/A3WG6 BK 00546 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 9500 Mpa | |
| bending strength | ISO 178 | 285 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.7 % |
| Flexural modulus | ISO 178 | 9200 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 185 Mpa |
| physical property | Test Condition | Test Method | BASF GERMANY/A3WG6 BK 00546 |
|---|---|---|---|
| Apparent density | 0.70 g/cm³ | ||
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 1.5 to 1.9 % |
| Mold Shrinkage - Constrained | 0.40 to 0.50 % | ||
| viscosity number | 96% H2SO4 | ISO 307 | 160 cm³/g |
| Melt volume flow rate | 275°C/5.0 kg | ISO 1133 | 10.0 cm3/10min |
| Shrinkage rate | 流量 | ISO 294-4 | 0.40 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 5.6 to 6.3 % |
| Shrinkage rate | 横向流量 | ISO 294-4 | 1.2 % |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/A3WG6 BK 00546 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 260 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 260 °C |
| Polymer Abbreviation | PA66-GF30 | ||
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 245 °C |
| injection | Test Condition | Test Method | BASF GERMANY/A3WG6 BK 00546 |
|---|---|---|---|
| drying time | 4.0 hr | ||
| Suggested maximum moisture content | 0.15 % | ||
| Temperature in the middle of the barrel | 290 °C | ||
| Temperature at the rear of the barrel | 290 °C | ||
| Processing (melt) temperature | 280 to 300 °C | ||
| Hopper temperature | 80 °C | ||
| drying temperature | 80 °C | ||
| Temperature at the front of the material cylinder | 290 °C | ||
| screw speed | < 18 m/min | ||
| Temperature | 80 to 90 °C | ||
| Spray nozzle temperature | 290 °C | ||
| Residence Time | < 10.0 min |