Material Properties:Low friction coefficient｜wear resistant｜Flame retardant
Application Areas:Fitness equipment｜Home appliance components｜Automotive Applications
Color:--
Grade:--

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	1.8 MPa, 未退火	ISO 75-2/A	271 °C
Heat Deflection Temperature	Heat Deflection Temperature	8.0 MPa, 未退火	ISO 75-2/C	129 °C
vicat		ISO 306/B50	227 °C
melting temperature		ISO 11357-3	350 °C

Impact resistance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	25 kJ/m²

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	横向流量	ISO 294-4	0.80 %
shrinkage rate	shrinkage rate	流量	ISO 294-4	0.0 %

injection	Test Condition	Test Method	Test Result
drying temperature			150 °C
drying time			6.0 hr
Suggested maximum moisture content			0.010 %
Hopper temperature			20 to 40 °C
Temperature at the rear of the barrel			345 to 355 °C
Temperature in the middle of the barrel			355 to 365 °C
Temperature at the front of the material cylinder			365 to 375 °C
Spray nozzle temperature			365 to 375 °C
Processing (melt) temperature			365 to 375 °C
mold temperature			80 to 140 °C
injection speed			快速
Back pressure			< 3.00 Mpa

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1A	8300 Mpa
tensile strength	断裂	ISO 527-2/1A/50	121 Mpa
Tensile strain	断裂	ISO 527-2/1A/50	3.0 %
flexural modulus	23°C	ISO 178	9500 Mpa
bending strength	23°C	ISO 178	152 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.