Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LCP S625 CELANESE USA
VECTRA®
Fitness equipment、Home appliance components、Automotive Applications
Low friction coefficient、wear resistant、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE USA/S625 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 25 kJ/m² |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/S625 |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-2/1A/50 | 3.0 % |
| bending strength | 23°C | ISO 178 | 152 Mpa |
| Flexural modulus | 23°C | ISO 178 | 9500 Mpa |
| tensile strength | 断裂 | ISO 527-2/1A/50 | 121 Mpa |
| Tensile modulus | ISO 527-2/1A | 8300 Mpa |
| physical property | Test Condition | Test Method | CELANESE USA/S625 |
|---|---|---|---|
| Shrinkage rate | 流量 | ISO 294-4 | 0.0 % |
| 横向流量 | ISO 294-4 | 0.80 % |
| Thermal performance | Test Condition | Test Method | CELANESE USA/S625 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 350 °C | |
| vicat | ISO 306/B50 | 227 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 271 °C |
| 8.0 MPa, 未退火，HDT | ISO 75-2/C | 129 °C |
| injection | Test Condition | Test Method | CELANESE USA/S625 |
|---|---|---|---|
| drying time | 6.0 hr | ||
| Suggested maximum moisture content | 0.010 % | ||
| Temperature in the middle of the barrel | 355 to 365 °C | ||
| Temperature at the rear of the barrel | 345 to 355 °C | ||
| Processing (melt) temperature | 365 to 375 °C | ||
| Hopper temperature | 20 to 40 °C | ||
| drying temperature | 150 °C | ||
| Temperature at the front of the material cylinder | 365 to 375 °C | ||
| Back pressure | < 3.00 Mpa | ||
| Temperature | 80 to 140 °C | ||
| injection speed | 快速 | ||
| Spray nozzle temperature | 365 to 375 °C |