PPA Zytel® HTN51G451HSL DUPONT USA
186
- Unit Price:US$ 5,017 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:40.5MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High temperature resistance｜High impact resistance｜Low temperature resistance｜Filler: Glass fiber reinforced material｜45% filler by weight
- Application Areas:Automotive interior parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | 23℃ | 125 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| horizontal | mm/mm/°C | 68.6E-5-127.0E-5 | |
| 1.8MPa, annealing | °C | 283to300 | |
| horizontal | mm/mm/°C | 63.5E-5-177.8E-5 | |
| 0.45MPa, Not annealed | °C | 273to312 | |
| RTI Imp | °C | 118to150 | |
| RTI Elec | °C | 140to150 | |
| flow | mm/mm/°C | 38.1E-5-50.8E-5 | |
| 1.8MPa, Not annealed | °C | 249to304 | |
| flow | mm/mm/°C | 185.4E-5-25.4E-5 | |
| mm/mm/°C | 195.6E-5-25.4E-5 | ||
| vicat | °C | 258to313 | |
| 8.0Mpa, Not annealed | °C | 165to230 | |
| 1.8MPa, Not annealed | °C | 247to292 | |
| 0.45MPa, annealing | °C | 296to320 | |
| 0.45MPa, Not annealed | °C | 275to308 | |
| RTI | °C | 119to150 | |
| Continuous use temperature | °C | 140to186 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index | % | 23to25 | |
| Burning wire flammability index | °C | 743to960 | |
| Hot filament ignition temperature | °C | 721to926 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 4.178to19.964 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | V | ||
| CTI | V |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 23℃,24hr | % | 0.30to0.51 | |
| Balance, 23 ℃, 50% RH | % | 0.21to1.2 | |
| Lateral flow: 23 ℃ | 横向, 23℃ | mm/mm | 119.4E-3-0.254 |
| 23℃,24hr | % | 0.12to0.30 | |
| Flow: 23 ℃ | 流动,23℃ | mm/mm | 48.3E-3-129.5E-3 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shear strength | 23℃ | 88.28to107.59 MPa | |
| Yield, 23 ℃ | 102.76to362.76 MPa | ||
| Poisson's ratio | 23℃ | 0.41 | |
| compressive strength | 23℃ | 142.76to196.55 MPa | |
| Yield, 23 ℃ | % | 1.4to2.5 | |
| Fracture, 23 ℃ | % | 1.5to3.1 | |
| % | 1.0to2.5 | ||
| Tensile modulus | 摩擦系数 | 0.15to0.52 | |
| Yield, 23 ℃ | 68.97to250.34 MPa | ||
| Fracture, 23 ℃ | 131.72to400.0 MPa | ||
| 162.76to199.31 MPa | |||
| Yield, 23 ℃ | % | 1.5to2.6 | |
| 12.62to270.34 MPa | |||
| Fracture, 23 ℃ | 108.28to262.76 MPa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.