TPE Hytrel® 6356 DUPONT USA
324
- Unit Price:US$ 4,835 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:51MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Thermal stability
- Application Areas:pipeline｜sheet｜Wire and cable｜Industrial applications｜Automotive sector｜Fitness equipment
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.22 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 9.0 g/10min | |
| Melt volume flow rate | ISO 1133 | 8.50 cm3/10min | |
| Shrinkage rate | ISO 294-4 | 1.5 % | |
| ISO 294-4 | 1.5 % | ||
| Water absorption rate | ISO 62 | 0.50 % | |
| ISO 62 | 0.60 % | ||
| ISO 62 | 0.20 % | ||
| MediumDensity | 1.06 g/cm³ | ||
| SpecificHeatCapacity of Melt | 2150 J/kg/°C | ||
| ThermalConductivityofMelt | 0.15 W/m/K |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | ISO 868 | 63 | |
| ISO 868 | 57 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB | |
| UL 94 | HB | ||
| IEC 60695-11-10,-20 | HB | ||
| IEC 60695-11-10,-20 | HB | ||
| Limiting Oxygen Index | ISO 4589-2 | 21 % | |
| FMVSS flammability | FMVSS302 | SE | |
| Fogging-G-value | ISO 6452 | 1E-04 g |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Emissions of Organic Compounds | VDA277 | 2.50 µgC/g | |
| Odor | VDA270 | 2.50 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 8256/1 | 300 kJ/m² | |
| Charpy Notched Impact Strength | ISO 179/1eA | 15 kJ/m² | |
| ISO 179/1eA | 25 kJ/m² | ||
| ISO 179/1eA | 120 kJ/m² | ||
| Impact strength of cantilever beam gap | ISO 180/1A | 19 kJ/m² | |
| ISO 180/1A | 81 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527-2 | 43.0 Mpa | |
| ISO 527-2 | 12.0 Mpa | ||
| ISO 527-2 | 15.0 Mpa | ||
| ISO 527-2 | 18.8 Mpa | ||
| ISO 527-2 | 19.0 Mpa | ||
| Tensile strain | ISO 527-2 | 31 % | |
| ISO 527-2 | >300 % | ||
| Nominal tensile fracture strain | ISO 527-2 | 500 % | |
| Tensile creep modulus | ISO 899-1 | 248 Mpa | |
| ISO 899-1 | 182 Mpa | ||
| Tensile modulus | ISO 527-2 | 280 Mpa | |
| tensile strength | ISO 527-2 | 20.0 Mpa | |
| Flexural modulus | ISO 178 | 290 Mpa | |
| wear resistance | ISO 4649 | 110 mm³ |
| elastomer | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tear strength | ISO 34-1 | 150 kN/m | |
| ISO 34-1 | 160 kN/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| relative permittivity | IEC 60250 | 4.10 | |
| Dissipation Factor | IEC 60250 | 0.012 | |
| IEC 60250 | 0.036 | ||
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Volume resistivity | IEC 60093 | 8E+13 ohms·cm | |
| dielectric strength | IEC 60243-1 | 20 KV/mm | |
| relative permittivity | IEC 60250 | 4.60 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/B | 80.0 °C | |
| ISO 75-2/A | 45.0 °C | ||
| brittle temperature | ISO 974 | -96.0 °C | |
| Glass Transition Temperature | ISO 11357-2 | 0.00 °C | |
| vicat | ISO 306/A50 | 195 °C | |
| ISO 306/B50 | 100 °C | ||
| melting temperature | ISO 11357-3 | 210 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 1.9E-04 cm/cm/°C | |
| ISO 11359-2 | 1.6E-04 cm/cm/°C | ||
| ASTME831 | 1.7E-04 cm/cm/°C | ||
| ISO 11359-2 | 1.8E-04 cm/cm/°C | ||
| ISO 11359-2 | 1.5E-04 cm/cm/°C | ||
| ISO 11359-2 | 5.44E-08 m²/s |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Contact Us
Get App