TPE 6356 DUPONT USA
Hytrel®
pipeline、sheet、Wire and cable、Industrial applications、Automotive sector、Fitness equipment
Thermal stability
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/6356 |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 25 kJ/m² |
| 23°C,局部断裂 | ISO 179/1eA | 120 kJ/m² | |
| -40°C | ISO 179/1eA | 15 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 81 kJ/m² |
| -40°C | ISO 180/1A | 19 kJ/m² | |
| 23°C | ISO 8256/1 | 300 kJ/m² |
| hardness | Test Condition | Test Method | DUPONT USA/6356 |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 63 |
| 邵氏D,15秒 | ISO 868 | 57 |
| Supplementary Information | Test Condition | Test Method | DUPONT USA/6356 |
|---|---|---|---|
| Odor | VDA270 | 2.50 | |
| Emissions of Organic Compounds | VDA277 | 2.50 µgC/g |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/6356 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 280 Mpa | |
| tensile strength | 10%应变 | ISO 527-2 | 15.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 31 % |
| Tensile creep modulus | 1000hr | ISO 899-1 | 182 Mpa |
| wear resistance | ISO 4649 | 110 mm³ | |
| tensile strength | 断裂 | ISO 527-2 | 43.0 Mpa |
| 50%应变 | ISO 527-2 | 18.8 Mpa | |
| 100%应变 | ISO 527-2 | 19.0 Mpa | |
| Tensile creep modulus | 1hr | ISO 899-1 | 248 Mpa |
| Nominal tensile fracture strain | ISO 527-2 | 500 % | |
| Tensile strain | 断裂 | ISO 527-2 | >300 % |
| Flexural modulus | ISO 178 | 290 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 20.0 Mpa |
| 5.0%应变 | ISO 527-2 | 12.0 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT USA/6356 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 20 KV/mm | |
| Volume resistivity | IEC 60093 | 8E+13 ohms·cm | |
| Dissipation Factor | 100Hz | IEC 60250 | 0.012 |
| relative permittivity | 100Hz | IEC 60250 | 4.60 |
| 1MHz | IEC 60250 | 4.10 | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.036 |
| flammability | Test Condition | Test Method | DUPONT USA/6356 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | IEC 60695-11-10,-20 | HB |
| 3.0mm | UL 94 | HB | |
| Fogging-G-value | condensate | ISO 6452 | 1E-04 g |
| UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | HB |
| FMVSS flammability | FMVSS302 | SE | |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 21 % |
| physical property | Test Condition | Test Method | DUPONT USA/6356 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 1.5 % |
| MD | ISO 294-4 | 1.5 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.60 % |
| 23°C,24hr | ISO 62 | 0.50 % | |
| MediumDensity | 1.06 g/cm³ | ||
| density | ISO 1183 | 1.22 g/cm³ | |
| Melt volume flow rate | 230°C/2.16kg | ISO 1133 | 8.50 cm3/10min |
| SpecificHeatCapacity of Melt | 2150 J/kg/°C | ||
| ThermalConductivityofMelt | 0.15 W/m/K | ||
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 9.0 g/10min |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.20 % |
| elastomer | Test Condition | Test Method | DUPONT USA/6356 |
|---|---|---|---|
| tear strength | 流量 | ISO 34-1 | 160 kN/m |
| 横向流量 | ISO 34-1 | 150 kN/m |
| Thermal performance | Test Condition | Test Method | DUPONT USA/6356 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：EffectiveThermalDiffusivity | ISO 11359-2 | 5.44E-08 m²/s |
| Glass Transition Temperature | ISO 11357-2 | 0.00 °C | |
| Linear coefficient of thermal expansion | TD：23to55°C | ASTME831 | 1.7E-04 cm/cm/°C |
| melting temperature | ISO 11357-3 | 210 °C | |
| Linear coefficient of thermal expansion | TD：-- | ISO 11359-2 | 1.8E-04 cm/cm/°C |
| MD：-40to23°C | ISO 11359-2 | 1.6E-04 cm/cm/°C | |
| TD：-40to23°C | ISO 11359-2 | 1.5E-04 cm/cm/°C | |
| MD：-- | ISO 11359-2 | 1.9E-04 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 80.0 °C |
| brittle temperature | ISO 974 | -96.0 °C | |
| vicat | -- | ISO 306/A50 | 195 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 45.0 °C |
| vicat | -- | ISO 306/B50 | 100 °C |