thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45MPa,未退火,3.20mm	ASTM D648	113 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,未退火,3.20mm	ASTM D648	77.2 °C
vicat		ASTM D15256	139 °C
Linear coefficient of thermal expansion	MD:-40到40°C	ASTME831	8.1E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40到40°C	ASTME831	1.1E-04 cm/cm/°C
RTI Elec		UL 746	50.0 °C
RTI Imp		UL 746	50.0 °C
RTI		UL 746	50.0 °C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.52mm	UL 94	HB

Impact resistance	Test Condition	Test Method	Test Result
Dart impact	-30°C,TotalEnergy	ASTM D3763	27.8 J
Dart impact	Dart impact	23°C,TotalEnergy	ASTM D3763	38.0 J

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	260°C/5.0kg	ASTM D1238	11 g/10min
shrinkage rate	MD：3.20mm	内部方法	0.80-1.2 %

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	屈服	ASTM D638	35.9 Mpa
tensile strength	tensile strength	断裂	ASTM D638	32.4 Mpa
elongation	屈服	ASTM D638	6.5 %
elongation	elongation	断裂	ASTM D638	200 %
flexural modulus	50.0mm跨距	ASTM D790	1550 Mpa
bending strength	屈服,50.0mm跨距	ASTM D790	51.7 Mpa
Tensile modulus		ASTM D638	1340 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.