Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PET X7110-NA9A005 SABIC INNOVATIVE US
XYLEX™
Automotive Applications
Flame retardant、High heat resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/X7110-NA9A005 |
|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 38.0 J |
| -30°C,TotalEnergy | ASTM D3763 | 27.8 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/X7110-NA9A005 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 1340 Mpa | |
| elongation | 断裂 | ASTM D638 | 200 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 51.7 Mpa |
| elongation | 屈服 | ASTM D638 | 6.5 % |
| tensile strength | 断裂 | ASTM D638 | 32.4 Mpa |
| 屈服 | ASTM D638 | 35.9 Mpa | |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 1550 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/X7110-NA9A005 |
|---|---|---|---|
| UL flame retardant rating | 1.52mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/X7110-NA9A005 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.80-1.2 % |
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 11 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/X7110-NA9A005 |
|---|---|---|---|
| vicat | ASTM D15256 | 139 °C | |
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 113 °C |
| RTI Imp | UL 746 | 50.0 °C | |
| RTI | UL 746 | 50.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 77.2 °C |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 8.1E-05 cm/cm/°C |
| RTI Elec | UL 746 | 50.0 °C |