PC LUPOY® 1301EP-30 LG CHEM KOREA

285

Unit Price:US$ 2,658 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
71MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance｜heat-resisting
Application Areas:electrical equipment｜Lighting applications
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

optical performance	Test Method	Test Result
Refractive index	ASTM D542	1.586
transmissivity	ASTM D1003	89.0 %
turbidity	ASTM D1003	0.70 to 1.5 %

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ASTM D256	无断裂

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6 mm	UL 94	V-2
	UL flame retardant rating	2.5 mm	UL 94	V-2
	UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	V-2
Hot filament ignition temperature	2.0 mm, 5.0 sec	IEC 60695-2-13	850 °C
UL flame retardant rating	0.50 mm	UL 94	V-2
Extreme Oxygen Index		ASTM D2863	26 %
Average degree of combustion		ASTM D746	3 CM

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ASTM D790	96.0 Mpa
Bending modulus		ASTM D790	2410 Mpa
elongation	Break	ASTM D638	150 %
elongation	elongation	Yield	ASTM D638	6.0 %
tensile strength	Break	ASTM D638	61.0 Mpa
tensile strength	tensile strength	Yield, 23°C3	ASTM D638	60.0 Mpa
Tensile modulus		ASTM D638	2340 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	-40 to 82°C，Flow	ASTM D696	6.8E-5 cm/cm/°C
Ball pressure temperature		IEC 60598-1	> 125 °C
Vicat softening temperature		ASTM D15255	144 °C
Hot deformation temperature	1.8 MPa, Annealed, 4.00 mm	ASTM D648	136 °C
	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm	ASTM D648	122 °C
	Hot deformation temperature	Hot deformation temperature	0.45 MPa, Annealed, 4.00 mm	ASTM D648	139 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 50% RH	ASTM D570	0.32 %
Water absorption rate	Water absorption rate	24 hr, 23°C	ASTM D570	0.15 %
Shrinkage rate	Flow	ASTM D955	0.50 - 0.70 %
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	30 g/10 min

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	2.00 mm	IEC 60112	V
Dissipation factor	60 Hz	ASTM D150	1.0E-3
Dielectric constant	60 Hz	ASTM D150	3.00
Dielectric strength		ASTM D149	17 KV/mm
Volume resistivity	23°C	ASTM D257	2.0E+17 ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC LUPOY® 1301EP-30 LG CHEM KOREA

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet