Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 1301EP-30 LG CHEM KOREA
LUPOY®
electrical equipment,Lighting applications
High impact resistance,heat-resisting
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG CHEM KOREA/1301EP-30 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D256 | 无断裂 |
| thermal performance | Test Condition | Test Method | LG CHEM KOREA/1301EP-30 |
|---|---|---|---|
| Ball pressure temperature | IEC 60598-1 | > 125 °C | |
| Heat Deflection Temperature | 1.8 MPa, 退火, 4.00 mm，HDT | ASTM D648 | 136 °C |
| vicat | ASTM D15255 | 144 °C | |
| Heat Deflection Temperature | 0.45 MPa, 退火, 4.00 mm，HDT | ASTM D648 | 139 °C |
| 1.8 MPa, 未退火, 4.00 mm，HDT | ASTM D648 | 122 °C | |
| Linear coefficient of thermal expansion | -40 到 82°C，流动 | ASTM D696 | 6.8E-5 cm/cm/°C |
| Mechanical properties | Test Condition | Test Method | LG CHEM KOREA/1301EP-30 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2340 Mpa | |
| elongation | 断裂 | ASTM D638 | 150 % |
| 屈服 | ASTM D638 | 6.0 % | |
| tensile strength | 断裂 | ASTM D638 | 61.0 Mpa |
| flexural modulus | ASTM D790 | 2410 Mpa | |
| tensile strength | 屈服, 23°C3 | ASTM D638 | 60.0 Mpa |
| bending strength | ASTM D790 | 96.0 Mpa |
| Electrical performance | Test Condition | Test Method | LG CHEM KOREA/1301EP-30 |
|---|---|---|---|
| dielectric constant | 60 Hz | ASTM D150 | 3.00 |
| Dissipation Factor | 60 Hz | ASTM D150 | 1.0E-3 |
| dielectric strength | ASTM D149 | 17 KV/mm | |
| Compared to the Leakage Tracking Index (CTI) | 2.00 mm | IEC 60112 | V |
| volume resistivity | 23°C | ASTM D257 | 2.0E+17 ohms·cm |
| optical performance | Test Condition | Test Method | LG CHEM KOREA/1301EP-30 |
|---|---|---|---|
| transmissivity | ASTM D1003 | 89.0 % | |
| refractive index | ASTM D542 | 1.586 | |
| Haze ratio | ASTM D1003 | 0.70 to 1.5 % |
| Physical properties | Test Condition | Test Method | LG CHEM KOREA/1301EP-30 |
|---|---|---|---|
| Water absorption rate | 24 hr, 23°C | ASTM D570 | 0.15 % |
| 平衡, 23°C, 50% RH | ASTM D570 | 0.32 % | |
| shrinkage rate | Flow | ASTM D955 | 0.50 - 0.70 % |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 30 g/10 min |
| flammability | Test Condition | Test Method | LG CHEM KOREA/1301EP-30 |
|---|---|---|---|
| UL flame retardant rating | 2.5 mm | UL 94 | V-2 |
| 3.0 mm | UL 94 | V-2 | |
| Hot filament ignition temperature | 2.0 mm, 5.0 sec | IEC 60695-2-13 | 850 °C |
| Average degree of combustion | ASTM D746 | 3 CM | |
| UL flame retardant rating | 0.50 mm | UL 94 | V-2 |
| 1.6 mm | UL 94 | V-2 | |
| Limiting Oxygen Index | ASTM D2863 | 26 % |