impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179	5.0	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179	100	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.8mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	2700	Mpa
tensile strength	Yield	ISO 527-2	55.0	Mpa
Tensile strain	Yield	ISO 527-2	7.5	%
Nominal tensile fracture strain		ISO 527-2	25	%
Bending modulus		ISO 178	2500	Mpa
bending strength		ISO 178	81.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature		ISO 11357-3	166	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	1.1E-04	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	156	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	95.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.39	g/cm³
melt mass-flow rate	190°C/2.16kg	ISO 1133	53	g/10min
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	46.0	cm3/10min
Shrinkage rate	MD：3.00mm		2.1	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.22	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	1E+16	ohms
Volume resistivity		IEC 60093	1E+14	ohms·cm
Dielectric strength	1.00mm	IEC 60243-1	36	KV/mm
Dielectric strength	Dielectric strength	3.00mm	IEC 60243-1	19	KV/mm
Compared to the anti leakage trace index		IEC 60112	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.