POM
POM MITSUBISHI THAILAND FX-11J
Injection grade
US$ 7,764 / MT
FOB Shenzhen Port
flammabilityTest ConditionTest MethodMITSUBISHI THAILAND/FX-11J
UL flame retardant rating0.8mmUL 94HB
mechanical propertiesTest ConditionTest MethodMITSUBISHI THAILAND/FX-11J
bending strengthISO 17881.0 Mpa
Nominal tensile fracture strainISO 527-225 %
tensile strengthYieldISO 527-255.0 Mpa
Bending modulusISO 1782500 Mpa
Tensile modulusISO 527-22700 Mpa
Tensile strainYieldISO 527-27.5 %
Electrical performanceTest ConditionTest MethodMITSUBISHI THAILAND/FX-11J
Dielectric strength3.00mmIEC 60243-119 KV/mm
Volume resistivityIEC 600931E+14 ohms·cm
Surface resistivityIEC 600931E+16 ohms
Dielectric strength1.00mmIEC 60243-136 KV/mm
Compared to the anti leakage trace indexIEC 60112PLC 0
Physical propertiesTest ConditionTest MethodMITSUBISHI THAILAND/FX-11J
Melt Volume Flow Rate (MVR)190°C/2.16kgISO 113346.0 cm3/10min
densityISO 11831.39 g/cm³
Water absorption rateEquilibrium,23°C,50%RHISO 620.22 %
Shrinkage rateMD：3.00mm2.1 %
melt mass-flow rate190°C/2.16kgISO 113353 g/10min
impact performanceTest ConditionTest MethodMITSUBISHI THAILAND/FX-11J
Charpy Notched Impact Strength23°CISO 1795.0 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179100 kJ/m²
thermal performanceTest ConditionTest MethodMITSUBISHI THAILAND/FX-11J
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B156 °C
Linear coefficient of thermal expansionTDISO 11359-21.1E-04 cm/cm/°C
MDISO 11359-21.1E-04 cm/cm/°C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A95.0 °C
Melting temperatureISO 11357-3166 °C