Material Description

Material Properties:Thermal stability｜Conductive｜Glass fiber reinforced
Application Areas:Electronic and Electrical Applications｜Fitness equipment
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	>100 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	>270 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB
Extreme Oxygen Index		ISO 4589-2	24 %

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield	ISO 527-2/50	70.0 Mpa
Tensile modulus		ISO 527-2/1	2700 Mpa
elongation	Yield3	ASTM D638	3.5 %
elongation	elongation	Break	ISO 527-2/50	>15 %
Bending modulus		ISO 178	2400 Mpa
bending strength		ISO 178	85.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
RTI Elec		UL 746	65.0 °C
thermal conductivity		ISO 8302	0.29 W/m/K
RTI		UL 746	65.0 °C
RTI Imp		UL 746	65.0 °C
Linear coefficient of thermal expansion	TD:23to60°C	ISO 11359-2	8E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD:23to60°C	ISO 11359-2	8E-05 cm/cm/°C
Ball Pressure Test	125°C	IEC 60695-10-2	通过
Vicat softening temperature	--	ISO 306/B120	200 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	210 °C
Hot deformation temperature	1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	60.0 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	180 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.6 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	10 %
Shrinkage rate	MD	Internal Method	1.1-1.5 %

Electrical performance	Test Condition	Test Method	Test Result
Dissipation factor	1MHz	IEC 60250	0.018
Compared to the anti leakage trace index	--	IEC 60112	PLC 0
Dissipation factor	60Hz	IEC 60250	5.8E-03
Dissipation factor	Dissipation factor	50Hz	IEC 60250	5.8E-03
Relative permittivity	1MHz	IEC 60250	3.00
	Relative permittivity	60Hz	IEC 60250	3.30
	Relative permittivity	Relative permittivity	50Hz	IEC 60250	3.30
Dielectric strength	3.20mm,in Oil	IEC 60243-1	16 KV/mm
Volume resistivity		IEC 60093	>1.0E+16 ohms·cm
Surface resistivity		IEC 60093	>1.0E+16 ohms
Compared to the anti leakage trace index	SolutionB	IEC 60112	PLC 0

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Sale	ISO 2039-2	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.