Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 B28N-BK1066 SABIC INNOVATIVE US
--
Electronic and Electrical、Fitness equipment
Thermal stability、Conductive、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/B28N-BK1066 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | >270 kJ/m² |
| -30°C | ISO 179/1eU | >100 kJ/m² |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/B28N-BK1066 |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 120 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/B28N-BK1066 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2700 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 70.0 Mpa |
| elongation | 屈服3 | ASTM D638 | 3.5 % |
| 断裂 | ISO 527-2/50 | >15 % | |
| bending strength | ISO 178 | 85.0 Mpa | |
| Flexural modulus | ISO 178 | 2400 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/B28N-BK1066 |
|---|---|---|---|
| relative permittivity | 60Hz | IEC 60250 | 3.30 |
| 50Hz | IEC 60250 | 3.30 | |
| Volume resistivity | IEC 60093 | >1.0E+16 ohms·cm | |
| dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 16 KV/mm |
| relative permittivity | 1MHz | IEC 60250 | 3.00 |
| Surface Resistivity | IEC 60093 | >1.0E+16 ohms | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案B | IEC 60112 | PLC 0 |
| Dissipation Factor | 50Hz | IEC 60250 | 5.8E-03 |
| 60Hz | IEC 60250 | 5.8E-03 | |
| 1MHz | IEC 60250 | 0.018 | |
| Compared to the Leakage Tracking Index (CTI) | -- | IEC 60112 | PLC 0 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/B28N-BK1066 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 3.0mm | UL 94 | HB | |
| Limiting Oxygen Index | ISO 4589-2 | 24 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/B28N-BK1066 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 1.1-1.5 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 2.6 % |
| 饱和,23°C | ISO 62 | 10 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/B28N-BK1066 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,100mm跨距，HDT | ISO 75-2/Ae | 60.0 °C |
| vicat | -- | ISO 306/B120 | 200 °C |
| thermal conductivity | ISO 8302 | 0.29 W/m/K | |
| Linear coefficient of thermal expansion | TD:23到60°C | ISO 11359-2 | 8E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,100mm跨距，HDT | ISO 75-2/Be | 180 °C |
| Linear coefficient of thermal expansion | MD:23到60°C | ISO 11359-2 | 8E-05 cm/cm/°C |
| vicat | -- | ISO 306/B50 | 210 °C |
| RTI Imp | UL 746 | 65.0 °C | |
| RTI | UL 746 | 65.0 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | 通过 |
| RTI Elec | UL 746 | 65.0 °C |