thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距	ISO 75-2/Af	157 °C
Linear coefficient of thermal expansion	流动 : 23 到 60°C	ISO 11359-2	6.3E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	横向 : 23 到 60°C	ISO 11359-2	1.1E-4 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	Flow	内部方法	0.50 %

injection	Test Condition	Test Method	Test Result
drying temperature			80 °C
drying time			4.0 hr
Temperature at the rear of the barrel			175 to 190 °C
Temperature in the middle of the barrel			195 to 205 °C
Temperature at the front of the material cylinder			210 to 220 °C
Processing (melt) temperature			200 to 215 °C
mold temperature			80 to 110 °C
Back pressure			0.200 to 0.300 Mpa
screw speed			30 to 60 rpm

mechanical properties	Test Condition	Test Method	Test Result
tensile modulus		ISO 527-2/1	7200 Mpa
tensile strength	断裂	ISO 527-2/5	104 Mpa
Tensile strain	屈服	ISO 527-2/5	2.3 %
flexural modulus		ISO 178	5500 Mpa
bending strength		ISO 178	122 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.