Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM KF004 BK SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Automotive Applications
heat-resisting,high strength,Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/KF004 BK |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 7200 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 104 Mpa |
| Tensile strain | 屈服 | ISO 527-2/5 | 2.3 % |
| bending strength | ISO 178 | 122 Mpa | |
| Flexural modulus | ISO 178 | 5500 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/KF004 BK |
|---|---|---|---|
| Shrinkage rate | Flow | 内部方法 | 0.50 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/KF004 BK |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : 23 到 60°C | ISO 11359-2 | 6.3E-5 cm/cm/°C |
| 横向 : 23 到 60°C | ISO 11359-2 | 1.1E-4 cm/cm/°C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距，HDT | ISO 75-2/Af | 157 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/KF004 BK |
|---|---|---|---|
| drying time | 4.0 hr | ||
| screw speed | 30 to 60 rpm | ||
| Temperature in the middle of the barrel | 195 to 205 °C | ||
| Temperature at the rear of the barrel | 175 to 190 °C | ||
| Processing (melt) temperature | 200 to 215 °C | ||
| drying temperature | 80 °C | ||
| Temperature at the front of the material cylinder | 210 to 220 °C | ||
| Back pressure | 0.200 to 0.300 Mpa | ||
| Temperature | 80 to 110 °C |