Material Description
- Material Properties:Flame retardant｜transparent
- Application Areas:Medical supplies｜Nursing supplies｜Non specific food
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 70 |
| R计秤 | ASTM D785 | 118 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | -- | ISO 306/A50 | 153 °C |
| -- | ISO 306/B50 | 141 °C | |
| -- | ISO 306/B120 | 142 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | MD：-40到95°C | ASTME831 | 6.8E-05 cm/cm/°C |
| MD：23到80°C | ISO 11359-2 | 7E-05 cm/cm/°C | |
| specific heat | ASTMC351 | 1250 J/kg/°C | |
| thermal conductivity | ASTMC177 | 0.19 W/m/K | |
| ISO 8302 | 0.20 W/m/K | ||
| RTI Elec | UL 746 | 130 °C | |
| Heat Deflection Temperature | 0.45MPa,Unannealed,100mmSpan | ISO 75-2/Be | 136 °C |
| 1.8MPa,未退火,6.40mm | ASTM D648 | 132 °C | |
| 1.8MPa,Unannealed,100mmSpan | ISO 75-2/Ae | 125 °C | |
| 0.45MPa,未退火,6.40mm | ASTM D648 | 137 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI Str | UL 746 | 130 °C | |
| vicat | ASTM D152510 | 154 °C |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ASTM D542 | 1.586 | |
| transmissivity | 2540µm | ASTM D1003 | 88.0 % |
| Haze ratio | 2540µm | ASTM D1003 | 1.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-2 | 25 % | |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Limiting Oxygen Index | ASTM D2863 | 25 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 63.0 J |
| 23°C | ASTM D3029 | 169 J | |
| Impact strength of cantilever beam gap | ASTM D1822 | 577 kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO 179/2C | 35 kJ/m² |
| Impact strength of cantilever beam gap | Colors | ASTM D256 | 800 J/m |
| Natural,Tints | ASTM D256 | 800 J/m | |
| 23°C | ASTM D256 | 800 J/m | |
| -30°C | ISO 180/1A | 10 kJ/m² | |
| 23°C | ISO 180/1A | 12 kJ/m² | |
| 23°C | ASTM D4812 | 3200 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| relative permittivity | 50Hz | IEC 60250 | 2.70 |
| 60Hz | IEC 60250 | 2.70 | |
| 1MHz | IEC 60250 | 2.70 | |
| Dissipation Factor | 50Hz | ASTM D150 | 9E-04 |
| 60Hz | ASTM D150 | 9E-04 | |
| 1MHz | ASTM D150 | 0.010 | |
| 50Hz | IEC 60250 | 1E-03 | |
| 60Hz | IEC 60250 | 1E-03 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.010 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| volume resistivity | ASTM D257 | >1.0E+17 ohms·cm | |
| IEC 60093 | >1.0E+15 ohms·cm | ||
| dielectric strength | 3.20mm,inAir | ASTM D149 | 15 KV/mm |
| 3.20mm,在油中 | IEC 60243-1 | 17 KV/mm | |
| dielectric constant | 50Hz | ASTM D150 | 3.17 |
| 60Hz | ASTM D150 | 3.17 | |
| 1MHz | ASTM D150 | 2.96 | |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 1 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Specific volume | ASTM D792 | 0.830 cm³/g | |
| density | ASTM D792 | 1.19 g/cm³ | |
| ASTM D792 | 1.20 g/cm³ | ||
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 11 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 10.0 cm3/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| Water absorption rate | 24hr | ASTM D570 | 0.15 % |
| 平衡,23°C | ASTM D570 | 0.35 % | |
| 平衡,100°C | ASTM D570 | 0.58 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 屈服 | ASTM D638 | 62.0 Mpa |
| 屈服 | ISO 527-2/50 | 63.0 Mpa | |
| 断裂 | ASTM D638 | 68.0 Mpa | |
| 断裂 | ISO 527-2/50 | 70.0 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| elongation | 断裂 | ASTM D638 | 130 % |
| Tensile strain | 断裂 | ISO 527-2/50 | 110 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 2340 Mpa |
| elongation | 屈服 | ASTM D638 | 7.0 % |
| flexural modulus | ISO 178 | 2300 Mpa | |
| Tensile modulus | ASTM D638 | 2370 Mpa | |
| ISO 527-2/1 | 2350 Mpa | ||
| bending strength | ISO 178 | 90.0 Mpa | |
| 屈服,50.0mm跨距 | ASTM D790 | 97.0 Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 10.0 mg |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.