PC/PBT

PC/PBT VALOX™ Resin 420SE0-BK1066 SABIC INNOVATIVE NANSHA

377

Unit Price:US$ 3,793 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
105MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:Trimming machine｜Food mixer motor stator and commutator｜Electric fan｜Laptop case｜Spool｜Switches｜ etc
Color:black
Grade:Injection grade

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus	1.3 mm/min, 50 mm span	ASTM D 790	9400 Mpa
bending strength	Break,1.3 mm/min, 50 mm span	ASTM D 790	186 Mpa
Rockwell hardness	R	ASTM D 785	119 -
Tensile modulus	5 mm/min	ASTM D 638	11500 Mpa
Tensile strength	Yield，类型L，5 mm/min	ASTM D 638	95 Mpa
Tensile strength	Tensile strength	Break，类型L, 5 mm/min	ASTM D 638	95 Mpa
elongation	Yield,类型L, 5 mm/min	ASTM D 638	1.2 %
elongation	elongation	Break，类型L, 5 mm/min	ASTM D 638	1.2 %
Bending modulus	1.3 mm/min, 50 mm span	ASTM D 790	9400 Mpa
bending strength	Break,1.3 mm/min, 50 mm span	ASTM D 790	186 Mpa
Rockwell hardness	R	ASTM D 785	119 -
Tensile modulus	5 mm/min	ASTM D 638	11500 Mpa
Tensile strength	Yield，类型L，5 mm/min	ASTM D 638	95 Mpa
Tensile strength	Tensile strength	Break，类型L, 5 mm/min	ASTM D 638	95 Mpa
elongation	Yield,类型L, 5 mm/min	ASTM D 638	1.2 %
elongation	elongation	Break，类型L, 5 mm/min	ASTM D 638	1.2 %
Tensile stress	抗张程度，Yield，类型L，5 mm/min	ASTM D 638	95 Mpa
	Tensile stress	抗张程度，Break，类型L, 5 mm/min，Yield	ASTM D 638	95 Mpa
		Tensile stress	拉伸伸长,Yield,类型L, 5 mm/min	ASTM D 638	1.2 %
		Tensile stress	Tensile stress	拉伸伸长,Break，类型L, 5 mm/min，Yield	ASTM D 638	1.2 %
Tensile modulus	拉伸模量,5 mm/min	ASTM D 638	11500 Mpa
Flexural Stress, brk	弯曲强度，Break,1.3 mm/min, 50 mm span	ASTM D 790	186 Mpa
Bending modulus	挠曲模量，1.3 mm/min, 50 mm span	ASTM D 790	9400 Mpa
Rockwell hardness	洛氏硬度 R	ASTM D 785	119 -

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	-40℃-4O℃, Flow	ASTM E 831	0.0000252 1/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	60℃-138℃, Flow	ASTM E 831	0.0000252 1/℃
Hot deformation temperature	0.45 MPa, 3.2 mm, Unannealed	ASTM D 648	212 °C
	Hot deformation temperature	1.82 MPa, 3.2mm, Unannealed	ASTM D 648	200 °C
		Hot deformation temperature	0.45 MPa, 6.4 mm，Unannealed	ASTM D 648	215 °C
		Hot deformation temperature	Hot deformation temperature	1.82 MPa, 6.4 mm, Unannealed	ASTM D 648	204 °C
Linear coefficient of thermal expansion	-40℃-4O℃, Flow	ASTM E 831	0.0000252 1/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	60℃-138℃, Flow	ASTM E 831	0.0000252 1/℃
Hot deformation temperature	0.45 MPa, 3.2 mm, Unannealed	ASTM D 648	212 °C
	Hot deformation temperature	1.82 MPa, 3.2mm, Unannealed	ASTM D 648	200 °C
		Hot deformation temperature	0.45 MPa, 6.4 mm，Unannealed	ASTM D 648	215 °C
		Hot deformation temperature	Hot deformation temperature	1.82 MPa, 6.4 mm, Unannealed	ASTM D 648	204 °C
Vicat softening temperature	维卡软化温度，等级 B/50	ASTM D 1525	200 °C
Hot deformation temperature	0.45 MPa, 3.2 mm, unannealed （未 Annealed）	ASTM D 648	212 °C
	Hot deformation temperature	1.82 MPa, 3.2mm, unannealed （Unannealed）	ASTM D 648	200 °C
		Hot deformation temperature	0.45 MPa, 6.4 mm， unannealed （Unannealed）	ASTM D 648	215 °C
		Hot deformation temperature	Hot deformation temperature	1.82 MPa, 6.4 mm, unannealed （Unannealed）	ASTM D 648	204 °C
Linear coefficient of thermal expansion	-40℃ to 4O℃,flow （Flow）	ASTM E 831	0.0000252 1/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	60℃ to 138℃, flow （Flow）	ASTM E 831	0.0000252 1/℃
Relative Temp Index. Elec	相对热指数，电性能	UL 746B	130 °C
Relative Temp Index, Meeh w/impact	相对热指数，机械冲击性能	UL 746B	130 °C
Relative Temp Index, Meeh w/o impact	相对热指数，非机械冲击性能	UL 746B	140 °C

Physical property type	Test Condition	Test Method	Test Result
Test project	测试条件	测试方法	测试结果测试单位

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792	1.3 g/cm³
Water absorption rate	23℃ 24hr	ASTM D570	1.3 %
Bi Rong		ASTM D 792	0.62 cm³/g
density		ASTM D 792	1.61 —
Shrinkage rate	Across Flow，3.2-4.6mm	SABIC method	0.6-1 %
	Shrinkage rate	Flow, 1.5-3.2 mm	SABIC method	0.3 - 0.5 %
		Shrinkage rate	Flow，3.2-4.6 mm	SABIC method	0.5 - 0.8 %
			Shrinkage rate	Across Flow ,1.5-3.2 mm	SABIC method	0.4 - 0.6 %
			Shrinkage rate	Shrinkage rate	Flow，3.2 mm	SABIC method	0.5 - 0.7 %
Water absorption rate	24 hours	ASTM D 570	0.06 %
density		ASTM D 792	1.61 —
Bi Rong		ASTM D 792	0.62 cm³/g
Water absorption rate	24 hours	ASTM D 570	0.06 %
Shrinkage rate	Flow，3.2 mm	SABIC method	0.5 - 0.7 %
	Shrinkage rate	Flow, 1.5-3.2 mm	SABIC method	0.3 - 0.5 %
		Shrinkage rate	Flow，3.2-4.6 mm	SABIC method	0.5 - 0.8 %
			Shrinkage rate	Across Flow ,1.5-3.2 mm	SABIC method	0.4 - 0.6 %
			Shrinkage rate	Shrinkage rate	Across Flow，3.2-4.6mm	SABIC method	0.6-1 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/PBT VALOX™ Resin 420SE0-BK1066 SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet Compare

Technical Data Sheet